螺旋钢管无论是在工业中有很大的用途，常见的参数有： 1、直度钢管的弯曲度不得超过钢管长度的0.2 ％。可从钢管侧表面的一端至另一端，平行于钢管轴线拉一根细绳或细金属丝，测量拉紧的细绳或细金属丝至钢管侧表面的最大距离。 2、钢管长度通常长度：6～12m。定尺长度：定尺长度应在通常长度范围内，其极限偏差为±500mm。 3、圆度在管端100mm长度范围内，钢管最大外径不得比标称外径大1 ％，最小外径不得比标称外径小1 ％。采用能够测量最大和最小外径的卡尺、杆规或其他测量工具测量。 4、管端钢管管端应加工坡口。坡口角度为30°，钝边尺寸为1.6mm±0.8mm。以钢管轴线的垂线为基准测量坡口角。尺寸理论重量kg螺旋钢管产品参数 静水压试验压力 Hydrostatil Test Pressuve MpaAPI Spec 5L 　　　　　　　　　　　GB/T9711-1997  ABX42X46X52X56X60X65X70L210L245L290L320L360L390L415L450L485φ21967891031.5236.6041.6346.6151.546.87.99.110.211.37.99.210.611.913.211.913.915.917.919.913.015.217.419.520.714.817.219.720.720.715.918.520.720.720.717.019.820.720.720.718.420.720.720.720.719.820.720.720.720.76.98.19.210.411.5 8.19.410.712.113.411.913.915.917.919.913.215.317.519.720.714.817.319.720.720.716.018.720.720.720.717.119.920.720.720.718.520.720.720.720.719.920.720.720.720.7φ27367891039.5145.9252.2858.6064.565.56.47.38.29.16.47.48.59.510.610.812.614.416.318.211.813.815.817.819.713.415.617.920.120.714.416.819.220.720.715.518.020.620.720.716.719.520.720.720.718.020.720.720.720.75.56.57.48.39.26.57.58.69.710.810.812.614.616.318.211.913.915.917.919.913.515.717.920.220.714.617.019.420.720.715.518.120.720.720.716.819.620.720.720.718.120.720.720.720.7φ32567891047.2054.9062.5470.1477.684.65.46.16.97.65.36.27.18.08.99.110.612.113.715.29.911.613.314.916.611.313.115.016.919.311.313.115.016.919.312.114.116.218.220.213.015.217.319.520.714.116.418.720.720.715.217.720.220.720.74.75.46.27.07.8 5.46.37.28.19.09.110.612.113.715.210.011.713.415.116.711.313.215.116.918.812.214.316.318.420.414.116.518.820.720.715.217.820.320.720.7φ37767891054.963.5772.8081.6890.514.04.65.35.66.64.65.46.16.97.77.89.210.511.813.18.610.011.412.914.39.711.313.014.616.2 10.412.213.915.717.411.213.114.916.818.712.114.116.218.220.213.115.217.419.620.74.04.76.36.06.74.75.56.27.07.87.89.210.511.513.18.710.111.513.014.49.711.413.014.616.210.612.314.115.817.611.213.115.016.818.712.214.216.218.320.313.115.317.519.720.7φ42667891062.1572.3382.4792.55102.593.54.14.75.25.84.14.85.46.16.86.98.19.310.411.67.68.910.111.412.78.610.011.512.914.39.210.812.313.915.49.911.613.214.916.510.712.514.316.117.911.613.515.417.319.33.54.14.75.35.94.14.85.56.26.96.98.19.310.411.67.78.910.211.512.88.610.111.512.914.49.310.912.514.015.69.911.613.214.916.610.812.614.416.218.011.613.515.517.419.4φ4786789101169.8481.3192.73104.10115.42126.693.13.64.24.75.25.13.64.24.85.46.16.76.27.28.39.310.311.36.87.99.010.111.312.4778.910.211.512.814.08.29.611.012.413.715.18.810.311.813.314.716.29.611.212.714.315.917.510.312.013.715.517.218.93.23.74.24.75.35.83.74.34.95.56.26.06.27.28.39.310.311.36.88.09.110.211.412.5 7.79.010.211.512.814.18.39.711.112.513.915.3 8.910.311.813.314.816.29.611.212.814.416.017.610.312.113.815.517.219.0φ5296789101177.3990.11102.79115.42127.99140.522.83.33.84.24.75.23.33.84.44.95.56.05.96.97.98.99.910.96.57.68.69.710.811.97.38.69.811.012.213.47.99.210.511.813.114.48.59.911.312.714.115.59.110.712.213.715.216.8 9.911.513.114.816.418.12.93.33.84.34.85.23.33.94.45.05.66.1 5.96.97.98.99.910.96.57.68.79.810.912.07.38.69.811.012.213.58.09.310.611.913.314.68.59.911.312.714.115.59.210.712.213.815.316.89.911.613.214.916.518.2φ6306789101192.53107.55122.72137.83152.90167.92 2.42.83.23.53.94.3 2.83.23.74.24.65.0 5.05.86.67.58.39.15.46.37.28.29.110.06.27.28.29.210.311.36.67.78.89.911.012.17.18.39.510.611.813.07.79.010.211.512.814.1 8.39.711.012.413.815.2 2.42.83.23.64.04.42.83.33.74.24.75.15.05.86.67.58.39.1 5.56.47.38.29.110.16.27.28.29.310.311.36.77.88.910.011.112.37.18.39.510.711.913.07.79.010.311.612.914.18.39.711.112.513.915.2φ72067891011105.65123.09140.47157.81175.1192.342.12.42.83.13.53.8 2.42.83.23.64.04.44.45.15.86.57.38.04.85.56.37.17.98.7 5.46.37.28.19.09.95.86.87.78.79.710.66.27.28.39.310.411.46.77.89.010.111.212.37.28.59.710.912.113.3 2.12.52.83.23.53.92.52.93.33.74.14.5 4.45.15.86.57.38.0 4.85.66.47.28.08.85.46.37.28.19.09.9 5.96.87.88.89.810.7 6.27.38.39.310.411.46.87.99.010.111.312.4 7.38.59.710.912.113.3φ82078910111213140.35160.2180.00199.76219.46239.22258.722.12.42.73.03.33.63.9 2.52.83.23.53.94.24.6 4.55.15.76.47.07.698.34.95.66.37.07.78.49.05.56.37.17.98.79.510.2 5.96.87.68.59.310.211.06.47.38.29.110.010.911.86.97.98.99.810.811.812.87.48.59.510.611.712.713.82.22.52.83.13.43.74.02.52.93.23.63.94.34.74.55.15.76.347.07.68.34.95.66.37.07.78.49.15.56.37.17.98.79.510.36.06.87.78.69.410.311.16.47.38.29.110.010.911.86.97.98.99.910.911.912.87.58.59.610.611.712.813.8φ9208910111213179.93202.20224.42246.59268.71290.782.22.42.73.03.23.52.52.83.13.53.84.14.55.15.76.26.87.45.05.66.26.87.48.15.66.34.07.78.49.16.06.87.68.39.19.86.57.38.18.99.710.57.07.98.89.610.511.47.68.59.510.411.312.32.22.52.73.03.33.62.62.93.23.53.84.24.55.15.76.26.87.45.05.66.36.97.58.15.66.37.07.78.59.26.16.97.68.49.29.96.57.38.18.99.110.67.07.98.89.710.611.47.68.59.510.411.412.3φ102091011121314224.39249.08273.72298.31372.84347.332.22.42.72.93.23.42.62.83.13.43.74.04.65.15.66.16.77.25.05.66.26.77.37.85.76.37.07.68.28.96.16.87.58.28.99.56.67.38.08.89.510.27.17.98.79.510.311.17.78.59.410.211.111.92.22.52.73.03.23.52.62.93.23.53.74.04.65.15.66.16.77.25.15.66.26.87.37.95.76.47.07.68.38.96.26.97.68.38.99.66.67.38.18.89.510.37.17.98.79.510.311.17.78.69.410.311.112.0φ122091011121314268.79298.40329.97357.49386.96416.381.82.02.22.42.62.92.12.42.62.83.13.33.94.34.75.15.66.04.24.75.15.66.16.54.85.35.86.46.97.45.15.76.36.87.48.05.56.16.77.37.98.65.96.67.37.98.69.36.47.17.88.69.310.01.92.12.32.52.72.92.22.42.72.93.13.43.94.34.75.15.66.04.24.75.25.76.16.64.85.35.86.46.97.45.25.86.36.97.58.15.56.16.77.38.08.66.06.67.38.08.69.36.47.27.98.69.310.0φ1420910111213313.18347.73382.23416.68451.081.61.71.92.12.31.82.02.22.42.63.33.74.04.44.83.64.04.44.85.24.14.65.05.55.94.44.95.45.96.44.75.25.86.36.85.15.76.26.87.45.56.16.77.38.01.61.82.02.12.31.92.12.32.52.73.33.74.04.44.83.74.14.54.95.34.14.65.05.55.94.44.95.45.96.44.75.35.86.36.85.15.76.36.87.45.56.16.87.48.0φ16201011121314397.05436.48476.48515.20554.491.51.71.82.02.11.82.02.12.32.53.23.53.94.24.53.53.94.24.64.94.04.44.85.25.64.34.75.15.66.04.65.15.56.06.45.005.56.06.57.05.45.96.47.07.51.61.71.92.02.21.82.02.22.42.53.23.53.94.24.53.63.94.34.65.04.04.44.85.25.64.34.85.25.66.14.65.15.56.06.55.05.56.06.57.05.45.96.57.07.5φ182012131415161718535.06579.32623.54667.51711.83755.90799.921.61.81.92.02.22.32.51.92.12.22.42.52.72.93.43.74.04.34.64.95.23.84.14.44.75.05.35.64.34.65.05.35.76.06.44.65.05.35.76.16.56.94.95.35.76.16.67.07.44.95.35.86.26.67.07.45.35.86.26.67.17.58.05.76.26.77.27.68.18.61.71.81.92.12.22.42.51.92.12.32.42.62.72.93.43.74.04.34.64.95.23.84.14.44.75.15.45.74.34.65.05.35.76.16.44.65.05.45.86.26.66.94.95.35.76.16.67.07.45.86.26.77.27.78.28.6以上为螺旋钢管产品参数

重轨孔型设计是制定型钢轧制工艺的重要内容之一。以人工经验为主的传统孔型设计过程,计算繁琐、原材料消耗大。为提高生产效率,缩短重轨新产品的设计周期,降低了轧机能耗和生产成本,本文采用参数化尺寸驱动思想设计实现了重轨孔型CAD系统。结合重轨孔型CAD系统的开发实例,提出将孔型标注参数化的重轨孔型CAD设计方法,介绍了Delphi环境下开发AutoCAD专业化应用的关键技术。 重轨参数 名称＝重轨 标准=GB/ 183-1963,GB/T 182-1963,GB/T 181-1963 ----------------------------------------------------------- 序号=1 钢轨型号\kg/m=38 A\mm=134 B\mm=114 C\mm=68 D\mm=13 截面面积\F\cm^2=49.5 重心距离\至轨底Z1\cm=6.67 重心距离\至轨顶Z2\cm=6.73 惯性矩\Jx\cm^4=1204.4 惯性矩\Jy\cm^4=209.3 截面系数\W1=Jx\Z1\cm^3=180.6 截面系数\W2=Jx\Z2\cm^3=178.9 截面系数\W3=Jy\(B/2)/cm^3=36.7 斜度\K=0.04375 理论重量\kg/m=38.733 通常长度\m=12.5，25 标准号=GB183-63 h1\mm=24 h2\mm=39 h3\mm=74.5 a\mm=27.7 b\mm=43.9 g\mm=79 f1\mm=9 f2\mm=10.8 f3\mm= r1\mm=13 r2\mm=4 r3\mm=4 S1\mm=56 S2\mm=110 S3\mm=160 φ=29 R\mm=300 R1\mm=7 R2\mm=7

铝青铜有较高的强度 杰出的耐磨性 用于强度比较高的螺杆、螺帽、铜套、密封环等，和耐磨的零部件,最杰出的特色便是其杰出的耐磨性。 　　含铝量一般不超越11.5%，有时还参加适量的铁、镍、锰等元素， 以进一步改 善功能。铝青铜可热处理强化，其强度比锡青铜高，抗高温氧化性也较好。为含有铁、锰元素的铝青铜有高的强度和耐磨性，经淬火、回火后可进步硬度，有较好的高温耐蚀性和抗氧化性在大气、淡水和海水中抗蚀性很好，可切削性尚可，可焊接不易纤焊，热态下压力制作杰出。目前我国已能量产。     国内常用的铝青铜牌号    QAL7，具有高的强度和弹性，在大气、淡水、海水和某些酸中耐蚀性高，可热、冷态压力制作，可电焊和气焊，不易钎焊。用于绷簧盒要求耐蚀的其它弹性元件。    QAL94，具有高的强度，杰出的减摩性和很好的耐蚀性，可热制作，可焊接，但不易钎焊。常用于高强、耐磨零件，如轴承、轴套、齿轮、涡轮等；还可制作接收嘴、法兰盘、扁形摇臂、支架等。    QAL1044，在400℃以下具有安稳的力学功能，有杰出的减摩性，在大气、淡水、海水中耐蚀性很好，可热制作，可焊接，但不易钎焊。常用于高强度的耐磨零件盒在400℃以下作业的零件，如轴承、轴套、齿轮、球形座、螺帽、法兰盘等。

电镀钨铜有什么功能特色    电镀前主张按电镀厂现有电镀技术电镀样品，电镀后的钨铜放置在真空炉内800°保温20分钟进行老化试验。假如出炉后钨铜并未呈现气泡、变色、等不良，阐明电镀技术没有问题，可按此技术进行下一步钨铜电镀，假如呈现气泡等问题，请与电镀供应商参议电镀技术问题。    钨铜是金属钨与金属铜结合在一起的二相“假合金”，因为钨金属与其他金属具有不相溶性，所以，钨铜合金的电镀比较困难。我公司结合多年经历，关于钨铜合金的电镀主张如下1、钨铜电镀前必定清洗，运用超声波+中性清洗液，将钨铜表面的氧化物质、油渍等脏化物质清洗洁净增强钨铜表面附着。清洗剂防止强酸强碱物质。2、清洗和电镀技术环节不能间隔时间过长，也就是说清洗后当即电镀。钨铜材料的功能    因为钨铜材料具有很高的耐热性和杰出的导热导电性，一起又与硅片、及陶瓷材料相匹配的热胀大系数，故在半导体材料中得到广泛的运用。适用于与大功率器材封装材料、热沉材料、散热元件、陶瓷以及基座等。钨铜电子封装和热沉材料，既具有钨的低胀大特性，又具有铜的高导热特性，其热胀大系数和导热导电功能能够经过调整钨铜的成分而加以改动，因此给钨铜供给了更广的用途。因为钨铜材料具有很高的耐热性和杰出的导热导电性，一起又与硅片、及陶瓷材料相匹配的热胀大系数，故在半导体材料中得到广泛的运用。    钨铜电子封装和热沉材料，既具有钨的低胀大特性，又具有铜的高导热特性，其热胀大系数和导热导电功能能够经过调整钨铜的成分而加以改动，因此给钨铜供给了更广的用途。因为钨铜材料具有很高的耐热性和杰出的导热导电性，一起又与硅片、及陶瓷材料相匹配的热胀大系数，故在半导体材料中得到广泛的运用。钨铜适用于与大功率器材封装材料、热沉材料、散热元件、陶瓷以及基座等。

硅石球磨机，顾名思义是用来研磨硅石的磨矿设备，除了硅石，它还可用于水泥、硅酸盐制品、金属和非金属选矿等。本文就从硅石球磨机的工作原理、特点、优势等方面为您展开介绍。 了解硅石 在介绍硅石球磨机之前，我们先来了解硅石的组分和用途。硅石可分为结晶硅石和胶结硅石，它是石英砂、石英岩、脉英石的总称，除此之外，硅石还伴有长石、云母等伴生物。经过加工后的硅石可得到硅酸钠和二氧化硅，硅酸钠的主要用途是制作硅酸盐，还可用于陶瓷、建材、玻璃、铁合金冶炼等行业。项目中的硅石球磨机 硅石球磨机结构 硅石球磨机主要由筒体、给料部、出料部、回转部、传动部(减速机，小传动齿轮，电机，电控)等主要部分组成，这些都与普通球磨机区别不大，这里我们要介绍的是硅石球磨机的特殊结构和部件，硅石球磨机配置有阶梯衬板或波纹衬板、小功率电机，合理的筒体、隔仓板、衬板设计，使每一块硅石都能得到充分研磨。 工作原理 硅石球磨机要求进料粒度≤25mm，出磨粒度为0.074-0.89mm，产量0.25~200t/h。当待磨硅石从入料端给入球磨机筒体内部，传动部会带动筒体缓慢转动，这时阶梯衬板或波形衬板就会起作用，配合设计合理的隔仓板和筒体内的构造，通过研磨介质的抛落，以及硅石与硅石、硅石与研磨体的摩擦，会将硅石最终研磨成小颗粒，从出料端排除。球磨机生产厂区 磨矿工艺 硅石的提纯过程需要经过擦洗—破碎磨矿—磁选—复选— 酸浸等工艺，新式选矿方法还有电选和生物选矿等，这其中破碎磨矿步骤对后续硅石的提纯骑着决定性作用，要尽量将硅石物料充分破碎，才能将杂质(伴生物)与硅石充分解离，才能帮助后续工序充分提纯，提升硅石成品品味。 硅石的磨矿工艺可选择湿磨和干磨，根据硅石原矿的特点来选择适当的工艺，湿磨的优势是能耗低、成品品味高，干磨的优势是节约水资源、工艺简单、成本低。当然选择那种工艺要通过选矿实验，结合物料性质来确定磨矿工艺。 硅石球磨机的特点 1、可针对贫矿率较高的硅石物料进行预选抛废的技术，降低能耗，提升成品品味; 2、硅石球磨机配备专用磨矿电机，易于启动，启动时间短、电力低; 3、采用波形或阶梯型衬板，能够对物料起到充分研磨的作用;   4、研磨介质的选择，搭配了超耐磨、超强超硬材质的钢球，钢球损耗低，节约成本。

典型的电解作业主要操作参数如下：同极距9.5～10.2cm，阴极表面电解液流速0.12m3/（h·m2），槽温40～46℃。虽然许多厂的电流密度仍在190～240A/m2，但是高的已达320～340A/m2。现在多数溶剂萃剂－电积厂的阴极铜纯度达到99.99%，甚至99.999%，高于可溶阳极法的产品。下表内列出两家大型电积厂的工作参数。 两家大型电积厂的工作参数工作参数圣曼纽尔恩昌加生产能力/t·a－166000167000电解槽数量/个 材料 衬里 长×宽×高/（m×m×m） 阳极，阴极数 巡查系统 清槽周期/d 酸雾控制 进液方式188 水泥 PVC 6×1.25×1.4 61，60 红外线 60 聚乙烯小球 底边盘管1120 水泥 Pb，6%Sb，PVC 4.6×1.1×1.4 41，40或61，60 目视 150 ф2cmPVC球 上部进液阳极成分/% 制造方法 长×宽×厚（mm×mm×mm） 同极距/cm 寿命/aPb98.7，Sn1.25，Ca0.06 冷轧 953×1160×6 9.5 10Pb93.9，Sb6.0 浇铸 880×1183×13 10 3阴极材料 长×宽×高（mm×mm×mm） 电积时间/d 铀板质量/kg不锈钢板 1000×1000×3 7 50铜始极片 950×950×0.8 4～10 23～38电解液富液成分 贫液成分 Co浓度/（mg·L－1） 单槽流量/（m3·min-1） 其他Cu42g/L，硫酸166g/L，41℃ Cu42g/L，硫酸170g/L，43℃ 100 0.2 Fe1.5g/L，Cl12mg/L，Mn 50mg/LCu 45g/L，硫酸136g/L，29℃ Cu 34g/L，硫酸150g/L，42℃ ≤200 0.02～0.3 Fe 0.8g/L能耗电流密度/（A·m－2） 电流效率/% 槽电压/V 槽电流/kA 吨铜直流电耗/kW·h00～300 93 ＞1.9 25～36 1900150～180 86～88 2.0 14～48 2000表中所列两家厂的铜产品质量都很好，杂质含量（10～4%）：玛格玛公司的圣曼纽尔厂，Pb＜1，S为2～3，Fe为2，Ni＜1，其他≤1；赞比亚恩昌加联合铜业公司（ZCCM），Pb≤10，S为15，Ca为2，Fe为10，Si为30，Ag为5，其他≤3。 另外需要提及的是许多电积新技术正在研究开发之中，值得注意，比如流态化电解槽等，不过，目前试验规模都还比较小。但是，最近有一种称作EMEW的筒状电解槽已经在澳洲进行试生产，操作情况和效果尚未见详细报道。

铍铜的性能及参数

 介绍钨铜的特性、运用以及参数钨铜特性:粉末冶金制造针对钨钢，高碳钢、耐高温超硬合金制造的模具需电蚀时，因普通电极损耗大，速度慢，钨铜是比较抱负材料．抗弯强度≥667Mpa钨铜使用:1.电极材料：使用于高硬度材料及溥片电极放电制作,电制作产品表面光洁度高,精度高,损耗低,有用节省.2.触点材料: 高中压开关或断路器的弧触头和真空触头，线路板焊接和电器接触点。3.焊接材料:埋弧焊机,气体维护焊机焊咀,无线电电阻厂(加工炭膜电阻,金属镀膜电阻)电阻对焊机碰焊材料(铜钨合金焊接圆盘)4.导卫材料:各种线材轧钢,用于导向维护效果材料,钨铜首要参数:牌号 密度(g/cm3) 硬度(HB) 电阻率(UW/cm) 电导率(%IACS)钨铜W50-Cu50 11.5-11.8 105-125 3.3-3.5 49-52钨铜W60-Cu40 12.5-13.5 130-150 3.5-4.5 35-46钨铜W70-Cu30 13.8-14.2 135-160 4.5-5.5 32-39钨铜W75-Cu25 14.5-14.9 170-200 5.0-6.0 30-38钨铜W80-Cu20 15.0-15.4 210-240 4.9-5.4 30-35钨铜标准板料规格表:100*100 (其它尺度需预定)(单位:mm)厚度 3 4 5 10 15 20 25 30 35 40 45 50钨铜标准圆棒规格表:长度100-300mm(其它尺度需预定)(单位:mm)外径Φ 3 4 5 6 8 10 12 15 20 25 30 35 40 45 50 55 60 

下面列举常用到的金矿浸出槽的一些参数供大家学习参考!

钨铜合金归纳了金属钨和铜的优势，其间钨熔点高(钨熔点为3410℃，铜的熔点1080℃)，密度大(钨密度为19.34g/cm3，铜的密度为8.89 g/cm3) ；铜导电导热功能优越，钨铜合金(成分一般规模为WCu7~WCu50)微观安排均匀、耐高温、强度高、耐电弧烧蚀、密度大；导电、导热功能适中，广泛运用于军用耐高温材料、高压开关用电工合金、电制作电极、微电子材料，做为零部件和元器材广泛运用于航天、航空、电子、电力、冶金、机械、体育器材等职业。 （1）军用耐高温材料 　　  钨铜合金在航天航空中用作、火箭发动机的喷管、燃气舵、空气舵、鼻锥，首要要求是要求耐高温(3000K~5000K)、耐高温气流冲刷才能，首要运用铜在高温下蒸发构成的发汗制冷效果(铜熔点1083℃)，下降钨铜表面温度，确保在高温极点条件下运用。（2）微电子材料 　　  钨铜电子封装和热沉材料，既具有钨的低胀大特性，又具有铜的高导热特性，其热胀大系数和导热导电功能能够经过调整钨铜的成分而加以改动，因此给钨铜供给了更广的用途。因为钨铜材料具有很高的耐热性和杰出的导热导电性，一起又与硅片、及陶瓷材料相匹配的热胀大系数，故在半导体材料中得到广泛的运用。适用于与大功率器材封装材料、热沉材料、散热元件、陶瓷以及基座等。（3）电制作电极 　　    电火花制作电极前期选用铜或石墨电极，廉价但不耐烧蚀，现在基本上已被钨铜电极代替。钨铜电极的优势是耐高温、高温强度高、耐电弧烧蚀，而且导电导热功能好，散热快。运用会集在电火花电极、电阻焊电极和高压放电管电极。 　　    电制作电极特点是种类规格繁复，批量小而总量多。作为电制作电极的钨铜材料应具有尽可能高的致密度和安排的均匀性，特别是细长的棒状、管状以及异型电极。（4）高压开关用电工合金 　　  钨铜合金在高压开关128kV SF6断路器WCu/CuCr中，以及高压真空负荷开关(12kV 40.5KV 1000A)，避雷器中得到广泛运用，高压真空开关体积小，易于保护，运用规模广，能在湿润、易燃易爆以及腐蚀的环境中运用。首要功能要求是耐电弧烧蚀、抗熔焊、截止电流小、含气量少、热电子发射才能低一级。除惯例微观功能要求外，还要求气孔率，微观安排功能，故要采纳特殊技术，需真空脱气、真空熔渗等杂乱技术

碘值 碘值是指活性炭在0.02N 12/KL水溶液中吸附的碘的量。碘值与直径大于10A 的孔隙表面积相关联, 碘值能够理解为总孔容的一个指示其器。 糖蜜值 糖蜜值是丈量活性炭在欢腾糖蜜溶液的相对脱色才能的办法。糖蜜值被解读为孔直径大于28A的表面积。由于糖蜜是多组分的混合物，有必要严厉依照阐明测验本参数。糖蜜值是用活性炭标样和要测验的活性炭的样品处理糖蜜液，经过核算过滤物的光学密度的比率而得。 堆积重 堆积重是丈量特定量炭的质量的办法。经过逐步把活性炭增加一个有刻度圆桶内至100cc，并丈量其质量。该值被用于核算填充特定吸附设备所需活性炭数量。简略地说，堆积重是活性炭每单位体积的分量。 颗粒密度 颗粒密度是每单位体积颗粒炭的分量，不包括颗粒以及大于0.1mm裂隙间的空间。颗粒密度是用置换来测定的。值是总孔容的指示器，是用饱满的零摄氏度的CCI4气流经过25度的炭床来丈量的。在规则的时刻距离内，丈量被吸附的CCI4的分量直到样品的分量改动能够忽略不计停止。 亚甲蓝 亚甲蓝值是指1.0克炭与1.0mg/升浓度的亚甲蓝溶液到达平衡状况时吸收的亚甲蓝的毫克数。 硬度 硬度是丈量活性炭机械强度的目标。分量的改动，用百分比表明。更切当地讲，硬度值是指颗粒活性炭在RO-TAP仪器中对钢球衰变运动的阻力。在炭与钢球触摸过今后，经过运用筛子上的炭的分量来核算硬度值。 磨损值 磨损值是丈量活性炭的耐磨阻力的目标。该实验丈量MPD的改动，经过百分比来表明。颗粒活性炭的磨损值阐明颗粒在处理过程中下降颗粒的阻力。它是经过在RO_TAP机器中将炭样品和钢球触摸，测定终究的颗粒均匀直径与原始颗粒的均匀直径的比率来核算的。 值 值是饱满空气与在特温度和特定的压力下经过炭床后，每单位分量的活性炭吸附的的量。 灰分 活性炭中包括无机物，一般是铝和硅。灰分是研磨成粉状的碳在954摄氏度时焚烧3个小时的剩下残渣。从技能视点看，灰分是活性炭矿藏氧化物的组分。一般界说为在一定量的样品被氧化后的分量百分比。 水分 水分是丈量碳所含水的多少。用Dean-Starktrap和冷凝器，在二溶液中煮沸活性炭来丈量水分。为了测验水分，水被冷凝和截留在待测定臂状容器内。活性炭的水含量也能够经过在150摄氏度下烘干3小时后活性炭分量上改动来测定。水分是活性炭中被吸附的水的分量的百分比。 关于不同用处的活性炭，经常用不同的物质和办法来查验它的吸附功能，如亚甲基蓝吸附值、碘吸附值、焦糖吸附值、硫酸奎宁吸附值等。其中亚甲基蓝吸附值是最常用的。亚甲基蓝是一种深蓝色染料，对它的吸附量反映了活性炭吸附小分子物质的才能;具有很多微孔的活性炭，此值较高。焦糖吸附值(或称焦糖脱色率、或糖蜜吸附率)是反映活性炭对具有较高分子量的有色物质的吸附功能，功能杰出的活性炭，此值到达100～110。 国内外制作的活性炭，都有一类称为“糖用活性炭”的产品，它可用于糖厂，也能够用在其他相似的职业，如葡萄糖溶液及味精溶液的精制脱色等。它的首要特点是具有较多的中孔，因而适于处理含有较多大分子有机物的溶液。这种活性炭的焦糖吸附值比较高。 我国“糖液脱色用活性炭”的国家标准(GB/T13803.3-1999)规则，活性炭产品分为优级品、一级品和二级品三种。其水分都低于10%;焦糖脱色率别离高于100、90和80，灰别离离低于3%、4%和5%(用磷酸法出产的活性炭可在7%～9%，不分等级)，酸溶物别离低于1%、1.5%和2%，还有铁含量和氯含量的规则。它们的pH值都在3～5之间。 活性炭的比表面积(BET)反映了每一克活性炭的总表面积的数值m2。它是用氮气或吸附法测出的。此值越大，活性炭的微孔越多，能够吸附更多的小分子物质。关于同一类的有机物，分子量较大者，被吸附较强;但这以它的分子能够进入活性炭的吸附孔为条件。当需求吸附的物质的分子量较高、分子尺度较大时，就要选用有较多中孔的活性炭。最理想的活性炭是具有很多刚好稍大于吸附物分子的孔道，假如孔道过大，总表面积就削减。分子量在300～100000之间的物质，相应的吸附孔径在0.5～4nm之间。 活性炭具有芳香环式的结构，长于吸附芳香族有机物(糖汁中的有色物大部分归于这类)，并长于吸附含有三个碳原子以上的其他有机物。它对不带电物质的吸附力较强，而对带电物质(如阴离子)的吸附较弱。对后者的吸附与溶液pH值有关：在酸性溶液中吸附较强，碱性溶液中较弱。由于弱酸性物质在低pH下带电较少以致不带电，较易被吸附;高pH下电荷较强，不利于吸附。为防止蔗糖转化，糖液用活性炭处理一般在中性下进行。活性炭对无机离子的吸附作用很弱，但用磷酸作活化剂的活性炭，及经过恰当羧基化处理的活性炭，也能吸附少数的金属离子。 活性炭的吸附作用和温度有关。关于大都的物理吸附作用，在低温下能够到达较大的吸附量，但吸附的速度较慢。在糖厂运用的大都情况下，活性炭和糖液触摸的时刻不长，故要求吸附进行得较快，就常用较高的温度，例如70～85℃。在这个温度下，一般经过15～30分钟(首要决定于糖液浓度)，活性炭的吸附作用就挨近其最大值。 活性炭的脱色作用与它的种类和处理的具体条件有极大的联系。在出产使用前要先经过实验室实验，挑选适合的活性炭种类和恰当的运用办法与技能条件。 粉状活性炭的粒子巨细是不均匀的，有些很微细的粒子或许穿过滤布。因而要选用恰当的过滤办法，必要时能够并用助滤剂如硅藻土，将它们和活性炭参加糖液中拌和恰当时刻后过滤。过滤机中构成的活性炭滤饼，能够调制成粉浆后参加深色的糖液中再用一次。 颗粒活性炭一般选用固定床吸附办法，行将颗粒活性炭装入圆筒形吸附柱中，糖液从上而下接连经过，与很多活性炭触摸，在底部出口处到达很高的脱色率。这种办法利于充分发挥活性炭的效能。近年又开发了新的接连的移动床体系。活性炭的再生一般是在洗糖后放入再生炉中高温加热，将吸附的有机物分化，亦能够用碱处理再生。

铁矿干选设备技术参数型号CTG～6162CTGCTG2CTGCTG2CTG给料料度（mm）0.5～01.01.5～01～00.5～01.0允许湿度%≤1≤2≤1≤2≤1≤2筒表场强qa145014501450145015001500筒体转速转/分404035352727处理能力t/w30～5030～5060～8060～80100～120100～120电机功率k/w1.51.5/1.52.22.2/2.244/4 备注：以上是我公司提供的铁矿干选设备的的特点和技术参数。生场现场位内蒙，可以实地进行考察

云锡摇床的技术参数 云锡摇床在使用后，应进行必要的维护和修理，因摇床各部件经常保持良好状况，不但能影响选矿性能和效率指标，而且能增长其寿命。 一、功能及使用范围云锡摇床的全套生产图纸资料是严格按照云南锡业公司的标准图纸所生产，该种摇床主要食用于各种有色金属使用。特别是对多有金属矿尤其能挥发它的奇效功能。它能选别2毫米以下的各种有色金属的重选与精选。经过多年的矿山生产实践证明，云锡摇床具有性能稳定、选矿效率高、平稳、噪音小和使用维修方便等特点，深受广大矿山用户的欢迎。 二、基本结构云锡摇床主要由床面、床头、溜动设备三大部分组成。床面由床架部分和给矿槽等部分组成，床面分有粗砂床面和刻槽床面。根据选矿粒度和浓度的不同选择适当的床面(见附表)。床面支撑在溜动设备上，由床头的床面挂钩连接床面，在床面的推动下使床面往复运动进行选矿。床头系采用偏心轴带动偏心滚轮来推动摇杆支臂，使摇杆支臂叉推动联结丁头螺杆，因而使螺杆往复运动。床头润滑轴承系采用ZQSN5-5-5材料作为滑动轴承，具有噪音小，转动灵活等特点，溜动设备部分主要是用来调节选矿设备所需要坡度，利用手轮调节斜度托板，使床面产生坡度。 三、主要技术参数名称规格技术性能床面尺寸4500×1850×1500mm摇床类别冲程（mm）冲次（次/分）总耗水量（M3/台日）处理量（T/台日）外形尺寸5454×1825×1242mm可调冲程8-22mm粗砂床16-22240-29019030配用电机Y90L-61.5千瓦绒砂床10-16300-320808总机重800公斤刻槽床10-16330-340505

1、电压 　　电泳涂装采用的是定电压法，设备相对简单，易于控制。电压对漆膜的影响很大；电压越高，电泳漆膜越厚，对于难以涂装的部位可相应提高涂装能力，缩短施工时间。但电压过高，会引起漆膜表面粗糙，烘干后易产生“橘皮”现象。电压过低，电解反应慢，漆膜薄而均匀，泳透力差。电压的选择由涂料种类和施工要求等确定。一般情况下，电压与涂料的固体分及漆温成反比，与两极间距成正比。钢铁表面为40～70V，铝和铝合金表面可采用60～100V，镀锌件采用70～85V。 　　2、电泳时间 　　漆膜厚度随着电泳时间的延长而增加，但当漆膜达到一定厚度时，继续延长时间，也不能增加厚度，反而会加剧副反应；反之，电泳时间过短，涂层过薄。电泳时间应根据所用的电压，在保证涂层质量的条件下，越短越好。一般工件电泳时间为1至3分钟，大型工件为3至4分钟。如果被涂物件表面几何形状复杂，可适当提高电压和延长时间。 　　3、涂料温度 　　涂料温度高，成膜速率快，但漆膜外观粗糙，还会引起涂料变质；温度低，电沉积量少，成膜慢，涂膜薄而致密。施工过程中，由于电沉积时部分电能转化成热能，循环系统内机械摩擦产生热量，将导致涂料温度上升。一般漆液温度控制在某些方面15～30℃。 　　4、涂料的固体分和颜基比 　　市售的电泳涂料的固体分一般为50%左右，施工时，需用蒸馏水将涂料固体分控制在10%～15%。固体含量太低，漆膜的遮盖力不好，颜料易沉淀，涂料的稳定性差。固体分过高，粘度提高，会造成漆膜粗糙疏松，附着力差。一般颜基比为1比2左右，高光泽电泳涂料的颜基比可控制在1比4。由于实际操作中，涂料的颜料量会逐渐下降，必须随时添加颜料分高的涂料来调节。 　　5、涂料的PH值 　　电泳涂料的PH值直接影响槽液的稳定性。PH值过高，新沉积的涂膜会再溶解，漆膜变薄，电泳后冲洗会脱膜。PH值过低，工件表面光泽不一致，漆液的稳定性不好，已溶解的树脂会析出，漆膜表面粗糙，附着力降低。一般要求施工过程中，PH值控制在7.5～8.5之间。在施工工程中，由于连续进行电泳，阳离子的铵化合物在涂料中积蓄，导致PH值的上升。可采用补加低PH值的原液，更换阴极罩蒸馏水，用离子交换树脂除去铵离子，采用阳极罩等方法降低PH值。若PH值过低时，可加入乙醇铵来调节。 　　6、涂料电阻 　　被涂物件从前一道工序带入电泳槽的杂质离子等引起涂料电阻值的下降，从而导致漆膜出现粗糙不均和针孔等弊病。在涂装施工中，需对涂料进行净化处理。为了得到高质量涂膜，可采用阴极罩设备，以除去铵及钙、镁等杂质正离子。 　　7、工件与阴极间距离 　　距离近，沉积效率高。但距离过近，会使漆膜太厚而产生流挂、橘皮等弊病。一般距离不低于20cm。对大型而形状复杂的工件，当出现外部已沉积很厚涂膜，而内部涂膜仍较薄时，应在距离阴极较远的部位，增加辅助阴极。

铜织造线的规格参数功能　    铜织造线的绕线式电动机正常运行时，三相绕组经过集电环引出的电阻短接。发动时，在转子绕组中串入一个发动电阻，到达了减小发动电流的意图。　　考虑到替换绕线式电动机后，尽管电机的发动功能得以改善，但并不能从根本上处理电机频频发动的问题，并且还需替换新电机，出资较大，节能效果并不抱负。因为发动电阻可逐段切除，恰当的串入发动电阻，能够使发动转矩到达电动机的最大转矩，缩短了发动进程。　　铜织造线有一中心支架，装有用若干绝缘片离隔的若干导电片。绝缘片不只有绝缘效果，并且其介电常数及面积和厚度挑选得使之能起到电容效果，用以按捺作业进程中的电流峰值。可用陶瓷材料制造导电片及绝缘片，这样能够获得杰出的耐磨功能。此外，导电片还能够用恰当高介电常数绝缘材料制造的环等离隔以构成电容。铜织造线和铜环绕线的异同之处从外形上看，铜织造线和铜环绕线的确比较相似，但事实上，两者的应用范围、特色等都是彻底不同的。为了让我们能够更好的区分其间的差异性，小编现已向织造线和环绕线的异同点罗列出来了。不管怎样，铜织造线和铜环绕新都能起到必定的屏蔽效果，并且能够依照不同的要求进行规划。可是因为所用原料不同，因而两者的实践应用范围也是不同的，铜织造线大都用在高频设备中，而铜环绕线却只能用在低频设备中，发挥各自的效果。比较看来的话，织造结构的线愈加安稳，不简单松懈，并且屏蔽是不受方向约束的。而铜环绕线则正好相反，不只简单松懈仍是有方向性。就手感而言，很明显就能够感觉到铜织造线比较硬，铜环绕线相对比较软。还有一部分差异体现在抗干扰性方面，也是铜织造线比较占优点。铜织造线具有哪些明显的功能　  铜织造线具有导电率高、抗疲劳能力强等特色，首要用于非水平方向的带电运动及中、低压断路器等。　　　　铜织造线的直流电阻率（20℃）不大于0.022Ωmm2/m,锡铜织造线的直流电阻率（20℃）不大于0.0234Ω.mm2/m。铜线软联接运用高、低压电器，真空电器，矿用防爆开关及轿车，机车及相关产品作软联接用。铜织造线选用祼铜线或镀锡铜线织造，用冷压办法制成，可依据用户要求镀锡、银。首要用于非水平方向的带电运动及中、低压断路器等。　　　　铜织造线选用铜织造线作为导体，两头选用铜管，铜管表面镀银处理，接头大小按客户配套尺度加工，再经过特殊处理，做成软联接，软接地，导电率高、抗疲劳能力强，可安全依据客户要求加工。铜织造线的编制办法有几种呢？　    依照编制办法来分类，铜织造带能够分为，斜纹、缎纹、平纹和杂纹几个类别。下面给我们介绍这几种类型的铜织造线的制造办法。　　　　首要，纱线经络筒、卷纬构成纬线管后，插在织造机的固定齿座上，纬纱管沿8字形轨迹反转移动，以牵引纱线彼此穿插织造。铜织造带一般锭数为偶数，织成带子为管状，锭数为奇数，织成的带子为扁片状。　　　　锭织技术旧中国就开端使用，锭数因设备不同，一般为9～100锭不等，织造的根本技术流程为：漂染—卷纬—织造—落机开剪—包装。1960年开端，对织造机进行屡次技术革新，首要有桃板直径扩大，设备断橡筋主动泊车设备，铁锭改为尼龙锭子。这些设备上的改善，使车速进步到160～190转/分，看台率增加一倍，产品质量大为进步。　　　　铜织造不只能够织带，还能够织绳。管状带便是织造绳的一种。直径为1～4厘米的称绳或绳线；直径大于4厘米的称为绳子；直径大于40厘米的称为缆或缆绳。       什么铜织造线？铜织造线应用范围是什么？铜织造线相关介绍有哪些？首要了解铜织造线概述：铜织造线选用优质软态圆铜线（0.10mm、0.15mm、0.20mm）或镀锡软态圆铜线（0.10mm、0.15mm、0.20mm），以多股（24、36、48锭）经单层或多层织造而成。其产品型号有TZ-20、TZX-20、TZ-15、TZX-15、TZ-10、TZX-10六种。　　铜织造线直流电阻率（20℃）不大于0.022Ω.mm2/m,镀锡铜织造线直流电阻率（20℃）不大于0.0234Ω.mm2/m。铜织造线及多股铜线都能够用超声波焊接，可是不能够镀锡，镀锡的话会影响超声波焊接。超声波金属焊接使用高频振荡波传递到两个需焊接金属表面，加压情况下，使两个金属表面彼此冲突而构成分子层之间熔合，其优势在于快速、节能、熔合强度高、导电性好、无火花、挨近冷态制作；缺陷所焊接金属件不能太厚（一般小于或等于5mm）、焊点位不能太大、需求加压。铜织造线　　铜织造线相关介绍之应用范围：　　铜、镀锡铜织造线首要用于电气设备、开关电器、电炉及蓄电池软联接线(JB/T6313.2-1992)铜织造线相关介绍之规格型号，见下表： 铜织造线规格型号标称截面(mm2 )结构组成  股数*根数*套数/单线直径 (mm)宽度不大于(mm)厚度不大于(mm)核算分量(kg/km )1624*22*1/0.20163.01662524*33*1/0.20183.52493524*44*1/0.20204.03315024*33*2/0.20225.04987024*44*2/0.20246.56649524*40*3/0.2020--90512024*40*4/0.2022--120715024*40*5/0.2024--150818524*40*6/0.2026--181024024*40*8/0.2030--241330024*40*8/0.2035--301640024*40*10/0.20+40--400436*44*2/0.20------50024*40*10/0.20+45--6500748*44*3/0.20------63024*40*10/0.20+50--6633448*44*5/0.20------80024*40*10/0.20+55---766148*44*7/0.20------  铜织造线相关介绍之铜织造线软联接选用铜织造线或铜绞线作为导体,两头联接处用铜管套上、压实,接头尺度按客户配套尺度加工,再经过特殊处理,做成软联接,软接地.导电率高,抗疲劳能力强.可彻底依据客户要求加工。　　铜织造线相关介绍之铜织造线软联接电流核算法：　　1.电流按客户需求一般1平方织造带，有效载荷电流4A核算，不相同截面积铜导电带参数都不相同，超大截面积可做多层或套　　2.类型分TZ/TZX-15，TZ代表紫铜，TZX代表镀锡铜，0.15代表单丝直径。　3.价钱首要取决于其时 铜价 钱和电流大小，一般按所做软联接长度计价。　　　铜织造线用无氧铜丝织造,线径0.10mm,0.12mm,0.15mm单丝,以多股（8、13、17、24、25、32、36、48锭）经单层或多层织造而成。线材部:电脑﹒电子﹒电器﹒轿车等周边联接线﹒端子线束制作﹒电子线材制作﹒电脑线材制作。可依据客户要求,柔软度,通电强度等特制而成.二端联接处选用无氧铜管限制而成,平坦,亮光。产品广泛使用于高低压电器，真空电器，高低压开关柜，电焊机，轿车，电力机车，电炉，矿用防爆电器，发电机组，碳刷导线特色:优势:柔软度好,易散热,耐曲折,导电率强,设备便利缺陷:超负荷能差一点,易碰坏中间铜丝。 

紫铜钢管是紫铜的一个种类，包括c1100紫铜钢管、T2进口紫铜钢管、T1紫铜钢管等，随着中国经济的发展，中国紫铜 行业 也是众多紫铜厂商关注的焦点之一。紫铜就是铜单质，因其颜色为紫红色而得名。紫铜就是工业纯铜，其熔点为1083℃，无同素异构转变，相对密度为8.9，为镁的五倍。比普通钢还重约15%。其具有玫瑰红色，表面形成氧化膜后呈紫色，故一般称为紫铜。它是含有一定氧的铜，因而又称含氧铜。1.紫铜钢管的性质紫铜，因呈紫红色而得名。它不一定是纯铜，有时还加入少量脱氧元素或其他元素,以改善材质和性能，因此也归入铜合金。中国紫铜加工材成分可分为：普通紫铜(T1、T2、T3、T4)、无氧铜（TU1、TU2和高纯、真空无氧铜）、脱氧铜（TUP、TUMn）、添加少量合金元素的特种铜（砷铜、碲铜、银铜）四类。紫铜的电导率和热导率仅次于银，广泛用于制作导电、导热器材。紫铜在大气、海水和某些非氧化性酸（盐酸、稀硫酸）、碱、盐溶液及多种有机酸（醋酸、柠檬酸）中，有良好的耐蚀性，用于化学工业。另外，紫铜有良好的焊接性，可经冷、热塑性加工制成各种半成品和成品。20世纪70年代，紫铜的 产量 超过了其他各类铜合金的总 产量 。紫铜中的微量杂质对铜的导电、导热性能有严重影响。其中钛、磷、铁、硅等显著降低电导率,而镉、锌等则影响很小。氧、硫、硒、碲等在铜中的固溶度很小,可与铜生成脆性化合物,对导电性影响不大，但能降低加工塑性。普通紫铜在含氢或一氧化碳的还原性气氛中加热时，氢或一氧化碳易与晶界的氧化亚铜(Cu2O)作用，产生高压水蒸气或二氧化碳气体，可使铜破裂。这种现象常称为铜的“氢病”。氧对铜的焊接性有害。铋或铅与铜生成低熔点共晶，使铜产生热脆；而脆性的铋呈薄膜状分布在晶界时，又使铜产生冷脆。磷能显著降低铜的导电性,但可提高铜液的流动性,改善焊接性。适量的铅、碲、硫等能改善可切削性。紫铜退火板材的室温抗拉强度为22～25公斤力／毫米2,伸长率为45～50％，布氏硬度（HB）为35～45。具有优良的导电性﹑导热性﹑延展性和耐蚀性。主要用于制作发电机﹑母线﹑电缆﹑开关装置﹑变压器等电工器材和热交换器﹑管道﹑太阳能加热装置的平板集热器等导热器材。常用的铜合金分为黄铜﹑青铜﹑白铜3大类。纯净的铜是紫红色的 金属 ，俗称“紫铜”、“红铜”或“赤铜”。 紫铜富有延展性。象一滴水那么大小的纯铜，可拉成长达两公里的细丝，或压延成比床还大的几乎透明的箔。紫铜最可贵的性质是导电性能非常好，在所有的 金属 中仅次于银。但铜比银便宜得多，因此成了电气工业的“主角”。2.紫铜钢管的用途紫铜的用途比纯铁广泛得多，每年有50%的铜被电解提纯为纯铜，用于电气工业。这里所说的紫铜，确实要非常纯，含铜达99.95%以上才行。极少量的杂质，特别是磷、砷、铝等，会大大降低铜的导电率。铜中含氧(炼铜时容易混入少量氧)对导电率影响很大，用于电气工业的铜一般都必须是无氧。铜管质地坚硬，不易腐蚀，且耐高温、耐高压，可在多种环境中使用。与此相比，许多其他管材的缺点显而易见，比如过去住宅中多用的镀锌钢管，极易锈蚀，使用时间不长就会出现自来水发黄、水流变小等问题。还有些材料在高温下的强度会迅速降低，用于热水管时会产生不安全隐患，而铜的熔点高达摄氏1083度，热水系统的温度对铜管微不足道。想要了解更多关于紫铜钢管的信息，请继续浏览上海 有色 网。 

钢管镀锌是提高钢管耐锈蚀性能、装饰美观的一种工艺手法。目前，最常用的钢管镀锌方法是热镀锌。无缝钢管的制造工艺可以分为：热轧（挤压）、冷轧（拔）、热扩钢管这基本的几类。焊管按照制造工艺可以分为：直缝焊接钢管，埋弧焊接钢管、板卷对接焊钢管，焊管热扩钢管。按照钢管的形状可以分为方形管、矩形管、八角形，六角形、D形，五角形等异形钢管。 复杂断面钢管，双凹型钢管，五瓣梅花形钢管，圆锥形钢管，波纹形钢管，瓜子形钢管，双凸形钢管等。按用途分类--管道用钢管、热工设备用钢管、机械工业用钢管、石油、地质钻探用钢管、容器钢管、化学工业用钢管、特殊用途钢管、其他。钢管生产技术的发展开始于自行车制造业的兴起。钢管不仅用于输送流体和粉状固体、交换热能、制造机械零件和容器，它还是一种经济钢材。用钢管制造建筑结构网架、支柱和机械支架，可以减轻重量，节省 金属 20～40％，而且可实现工厂化机械化施工。钢管对国民经济发展和人类生活品质的提高关系甚大，远胜于其他钢材。从人们的日常用具、家具、供排水、供气、通风和采暖设施到各种农机用具的制造、地下资源的开发、国防和航天所用枪炮、子弹、导弹、火箭等都离不开钢管。钢管镀锌能有效地延长钢管的腐蚀时间，使得钢管的利用价值得到提升，目前钢材 市场 的镀锌钢管的 价格 也在小幅度的上涨。 

涂敷钢管是在大口径螺旋焊管和高频焊管基础上涂敷塑料而成，最大管口直径达1200mm，涂敷钢管可根据不同的需要涂敷聚氯乙烯（PVC）、聚乙烯（PE）、环氧树脂（EPOZY）等各种不同性能的塑料涂层，附着力好，抗腐蚀性强，可耐强酸、强碱及其它化学腐蚀，无毒、不锈蚀、耐磨、耐冲击、耐渗透性强，管道表面光滑，不粘附任何物质，能降低输送时的阻力，提高流量及输送效率，减少输送压力损失。涂层中无溶剂，无可渗出物质，因而不会污染所输送的介质，从而保证流体的纯洁度和卫生性，在-40℃到+80℃范围可冷热循环交替使用涂敷钢管，不老化、不龟裂，因而可以在寒冷地带等苛刻的环境下使用。大口径涂敷钢管广泛应用于自来水、天然气、石油、化工、医药、钢管、通讯、电力、海洋等工程领域。

一、电炉设计的计算程序     电炉变压器功率的确定；     二次电压的选择及确定。     炉子主要尺寸的确定：     1、电极直径及电极分布直径的确定；     2、炉床面积的确定；     3、电炉炉膛高度的确定。     （一）电炉变压器功率的确定     电炉功率按电炉每昼夜处理物料量以及每吨物料耗电量计算，其计算公式如下：                                          （1）     式中P—炉用变压器的总功率，kVA；         A—电炉炉料的单位耗电量，kW·h/t料；         Q—昼夜处理固体炉料量, t/d;         K1—功率利用系数，一般为0.9～0.975;         K2—时间利用系数，一般为0.92～0.95;         cosφ—功率因数，一般为0.9～0.98。     当选用3台单相变压器供电时，每台的功率为总功率1／3。     功率利用系数K1在炉用变压器选择恰当时可以达到1.0。当炉渣电导率与操作电压不相适应或作业制度不当时往往小于1.0。一般可取0.9～0.975。     时间利用系数K2与停电时间直接相关，停电原因主要是清扫短网，变换操作电压（变压器不是带负荷调压的）和电极事故，此外，还应考虑下放电极降低负荷的影响。     功率因数cosφ取决于接线方法，同时随炉子的负荷降低操作电压的提高而增加。图1为芬兰依玛特拉厂9000kVA电炉的电压及负荷铜cosφ的关系。为了提高功率因素可安设电容器或将电炉与其它设备连接。例如乌干达今贾厂将电炉同转炉高压鼓风机的同步电动机连接，以提高功率因数。图1  依玛拉特厂9000kVA电炉电压及负荷与cosφ的关系     （二）二次电压的选择     目前尚无准确的矿热电炉的二次电压计算方法，可根据炉子特性、炉渣成分、炉子功率等因素结合类似工厂的实际经验和数据来选择。由于生产中原料成分可能变化，通常炉用变压器要作成8～15级以适应操作功率和炉渣性质的变化，级间差20～40V。     二次电压可按下述公式估算：     1、按经验公式                                       （2）     式中 —炉用变压器的二次电压，V；       —每根电极的功率，kVA，三级电炉每根电极的功率为炉子额定功率的1/3，六极电炉每根电极的功率为炉子额定功率的1/6。     K和n值列于表1。 表1  K和n值熔炼性质Kn①三极六极熔炼成铜锍14190.35渣用电热前床7.58.40.41     ①近年来，有些国家和工厂趋向于采用高电压操作，获得较好技术经济指标。表中经验数据应予提高，对铜镍精矿或矿石熔炼，n值可达0.29～0.32；对铜精矿熔炼，n值可达0.392。     2、按圆周电阻系数计算     当渣型和温度一定时：                                  （3）     式中 —电极直径，cm；       —每根电极端部对炉底的电阻，Ω，   —圆周电阻系数，Ω·cm，由实验却确定。     铜锍熔炼电炉内 一般为2.06     电极对炉底的电压（相电压）按下式确定：                                       （4）     式中 —相电压V；       —每根电压的功率，kVA。     变压器的二次额定电压 为：     对单相六极电炉：                               （5）     对三相三极或六极电炉：                               （6）     式中 —电炉电效率，一般为0.95～0.96；         X—短网感抗，Ω。     因一般电炉感抗很小，上两式可简化为：     对单相六极电炉：                                      （7）     对三相三极或六极电炉：                                     （8）     3、按每根电极的熔池电阻计算（ ）                          （9）     式中 —每根电极的熔池电阻，Ω；        —渣层厚度，cm；        —电极插入渣层深度，cm；          —炉渣在熔池平均温度下的电导率，Ω-1·cm-1，在条件许可时应测定工艺选择的某种渣型的电导率，或按表2、表3选取其近似值。       —考虑熔池内固体物理分布情况及电极插入深度的系数，见表4。      —考虑电极工作端形状的系数，见表5。     由公式9求出 后，再按公式5或公式6计算变压器二次电压。 表2  高铁炉渣的物理化学性质测定数据（一）编号炉渣成分，%熔点℃热含1200℃  kJ/g粘度，10-1Pa·sSiO2FeOAl2O3CaOMgO1250℃1200℃1160℃134.0952.754.643.161.0710901.471.22.54.6236.3448.156.842.381.2310051.211.62.82.2337.7650.214.391.461.3511001.221.72.84.0440.0841.412.962.091.1011202.081.72.95.7542.1139.414.181.791.2511602.102.65.421.8 续表2  高铁炉渣的物理化学性质测定数据（二）编号电导率，Ω-1cm-1表面张力，N/m密度，t/m31250℃1200℃1160℃1250℃1200℃1160℃1250℃1200℃1160℃10.30.280.210.3500.3670.3983.353.433.5020.190.110.090.3300.3430.3603.153.283.3530.270.220.180.3270.3350.3483.253.323.4040.170.140.120.3050.3160.3243.153.203.3050.0060.0610.0520.2840.2860.2952.783.053.20 表3  高钙镁炉渣的物理化学性质测定数据（一）编号炉渣成分，%熔点℃热含1250℃  kJ/g硅酸度密度，t/m3FeOSiO2CaOMgOAl2O3111.5140.2217.3811.5510.4612001.441.763.27215.3741.7517.0911.399.7312201.391.733.32317.8443.2515.819.749.1611801.321.863.36419.6241.4915.775.569.1511701.431.743.55521.8639.2815.699.049.0911401.421.623.45611.4336.7620.8813.1711.3012001.411.423.29718.0934.4817.5211.7710.3612001.431.333.43820.0034.6719.2911.4610.2111701.331.323.46922.5133.7516.4710.4110.9311701.511.303.561024.6432.0315.7510.1810.3211801.381.223.571110.8441.8420.8012.408.3312101.511.493.261216.3243.1817.0911.218.0912201.431.783.331318.9942.4015.9210.957.4311701.471.723.371412.5438.2221.5913.389.1812001.511.203.291517.1337.7618.6612.638.5411951.481.423.421619.8537.4718.6111.658.0711751.391.373.411723.3835.3117.1612.757.5511701.501.193.51 续表3  高钙镁炉渣的物理化学性质测定数据（二）编号粘度，10-1Pa·s电导率，Ω-1cm-11260℃1280℃1300℃1320℃1330℃1340℃1260℃1280℃1300℃1320℃1330℃1340℃133.426.221.017.215.714.80.0440.0500.0580.0680.0780.10231.616.012.49.4329.013.810.79.49.19.00.0760.1020.1230.1380.1460.160416.011.37.85.24.43.60.0760.0830.1000.1280.1700.215517.414.010.98.67.97.20.0650.0710.0880.1390.193635.025.020.016.214.513.00.0480.0520.0540.0550.056720.814.510.98.88.30.0790.0980.1200.16587.45.03.62.60.0840.0940.1120.1430.165920.912.37.95.65.04.80.0820.0980.1230.1460.1651013.04.94.23.43.22.81116.012.09.57.67.06.41214.611.910.108.58.07.5139.88.57.26.05.44.81423.015.810.67.67.06.60.0760.0850.1101542.026.017.712.310.38.50.0840.112165.64.43.32.52.21.90.1320.172177.05.64.53.83.73.60.1020.1260.160表4  电极插入熔池深度的系数表物料分布特点当 为下列数值时的系数炉料至电极表面距离料堆沉入渣层深度0.250.5接近电极直径011大于电极直径＜11炉料完全覆盖熔池表面1.2炉料完全覆盖熔池表面＞1.3表5  电极工作端形状的系数表0.2511.5平端头圆柱形电极1.51.752具有锥体高度为 的锥形电极111     （三）二次电压级的确定     以上计算的额定电压只能反映某一特定条件的合理电压值。实际上，物料条件及操作条件常有变化，因此，在确定变压器的二次电压时，应有一定的调节范围，另外，为适应开炉期低负荷运行的需要，还可以在低功率范围内按恒定电流条件设计，即变压器具有恒功率和恒电流两个工作范围。炉用变压器功率及二次电压，见图2。图2  炉用变压器功率及二次电压     图中， 为额定工作电压（或计算电压）， 及 分别为变压器额定功率时的调压范围， 为功率下降后（恒电流工作段）的最低电压。炉用变压器的 、 及 电压值可列式计算：=（1.1～1.25）                                     （10）=（0.1～0.8）                                     （11）=0.5                                           （12）     变压器恒功率段内的电压级按下式确定：                                     （13）     变压器恒电流段的电压级数按下式确定：                                        （14）     式中 、 为额定电压级数的电压差，其值见表6。 表6  功率与级差伏数值功率范围，kVA恒电流段，V恒功率段，V1000以内5～108～121000～600010～1515～256000以上15～2018～35     注：变压器调压方式有无载调压和有载调压两种。新设计的大型矿热电炉炉用变压器多采用有载调压。     云冶电压级：1号电炉变压器电压级为8级，级差为20V；     2号电炉变压器电压级为27级，级差为15V。     变压器的二交电压的切换，中小型电炉采用无载切换方式，大型电炉采用有载调压切换方式，即改变电压时，可以在带电的情况下进行工作。     （四）炉子主要尺寸的确定     1、电极直径及电极分布直径的确定     电极直径是根据功率和选定的电压以及电极截面上的单位电流密度选定的。     （1）电极直径可按以下公式计算：     按电流强度计算                                     （15）     按炉子功率计算     三相电炉                                            （16）     六极单相电炉                                        （17）     式中 —电极直径，cm；        —电极内最大电流强度，A；        —电极内单位电流密度，A/cm2,见表7。        —炉子额定功率，kVA；        —炉子额定功率时的最小电压，V。 表7  几种不同类型电炉的自熔电极电流密度炉子用途不同直径电极的电流密度，A/cm2＜600mm＜900mm＜1200mm铜锍电炉4～53～42～3.5炼镍铁电炉5～63.5～4.53～4电热前床2.5～32～2.5    16、17公式未考虑电极工作时的消耗速度。自焙电极的电极消耗速度不应超过电极糊的烧结速度，否则将产生“软断”的严重事故。因此，按上述公式计算出电极直径后，还必须验算每日电极下放长度（ ），若 大于电极烧结速度 （m/d），则直径不符合要求，必须增大 使 下降，直至 ＜ 为止。    与电极糊种类、质量、炉顶温度等因素有关，对熔炼铜镍锍或铜锍的电炉， =0.35～0.45m/d。    按下式公式计算：                                （18）     式中 —每日电极下放长度，m/d；        —烧结后电极糊的堆积密度，t/m3；        —电极直径，cm；         m—电极根数；         K2—时间利用系数，一般为0.92～0.95；         —每1000kW·h电能消耗需要耗用的电极糊重量，t/1000kW·h。     自焙电极的电极糊消耗量（ ）实践的经验数据见表8。 表8  自焙电极电极糊单耗经验数据熔炼过程的特点，kg/1000 kW·h铜硫化物精矿熔炼4～4.6（高达10）铜镍硫化矿石或精矿熔炼4.1～6.2氧化镍矿石熔炼9～11转炉渣贫化5～8kg/t渣     （2）电极分布直径     根据电极直径可确定电极分布直径，即可确定排成一条直线的电极中心间距离或沿电极中心通过的圆周直径，后者电极配置在三角形顶点内：                                      （19）     式中 —电极分布直径，cm；        —电极直径，cm；         —确定电极分布直径时的系数，见表9。 表9  确定电极分布直径时的系数炉子用途及型式K值长方形铜锍电炉2.7～3.2长方形电热前床3～4圆形电热前床3～3.5长方形贫化电炉2.5～3.0     2、炉床面积的确定     （1）对于圆形电炉炉床面积为：                                       (20)     式中  F—圆形电炉床面积，m2；            D—圆形电炉的内径，m；            D= +（4.4～5）                                  （21）          —电极直径，m；          —电极分布直径，m。     （2）对于长方形电炉炉床面积为：     ①按经验计算炉床面积： F=BL                                            (22)     式中  F—炉床面积，m；           B—炉膛宽度，m，按下列经验公式确定：                B=K宽d极，m                                       （23）         K宽—系数，见表10。 表10  系数K宽值名称K宽长方形熔炼电炉5～6长方形贫化电炉或电热前床没有水冷炉壁时6～7有水冷炉壁时4.8～5.5         —电极直径，m；          L—炉膛长度，m，按下列经验公式确定：           对于三极电炉：L=(12～13)                                 (24)           对于六极电炉：L=(19～21)                                   (25)     也可用下式计算：        L=(m-1)＋（2.5～3） +（3.2～3.6）                     （26）     以上式中符号意义同前。     电炉炉膛宽度B也用以下方法计算：     当为长方形电炉时，其炉床宽度与长度之比可以取为：     三极电炉：1∶2.2   六极电炉：1∶4     由此，炉宽为： 或 ，m     炉床尺寸和电极直径之比可在电极有效区对炉墙有影响的位置进行检查。     实际上，入炉墙到电极中心的最小距离小于（2.5～2.8）d（长方形电炉），（2～2.5）d（圆形电炉），则长方形电炉宽度可为：（5～5.6）d，而圆形电炉直径可为 +（4.4～5）d，这样，可以保证炉墙寿命。     图3为三极电炉简图。图3  三极电炉简图 1－放锍端；2－放渣端     ②按单位面积功率计算炉床尺寸：,m2                                     （27）     式中 —炉子单位功率，kVA/m2；          —炉子功率，kVA；          可依据炉子额定功率按下式计算：                                        （28）     式中 及 同上公式，K和n为系数。     不同操作过程和不同型式的炉子的K和n系数值列于表11。 表11  不同操作过程和不同型式的炉子的系数K和n值操作过程和炉渣型式Kn长方形电炉熔炼成铜锍40.35圆形电炉熔炼成铜锍80.35渣用长方形电热前床279-0.18i①     ①在这种情况下，幂指数是负数，因为单位功率是随着炉子功率的增加而降低。     目前炉膛单位面积功率实践经验为100～400kVA/m2。     3、电炉炉膛高度的确定                               （29）     式中 H—炉膛高度，m；          h1—铜锍层厚度，m，一般为0.7～0.8；          h2—渣层厚度，m，一般为1～1.5；          h3—料层厚度，m，一般为0.3～0.6；          h4—气体空间高度（料坡顶至拱顶中心），m，以保证炉膛内气体流速2～4m/s为宜。     二、电炉设计参考图     云冶30000kVA铜冶炼电炉见图4。     国内外铜熔炼电炉主要参数见表12。     云冶电炉炉用变压器技术规格及变压器特性实例见表13、表14。图4  30000kVA铜冶炼电炉 1－排烟口；2－出渣口；3－放铜口；4－加料口 表12  国内外铜熔炼电炉主要参数（一）厂别电炉功率kVA单位功率kVA/m2变压器台数二次电压V炉子尺寸，m炉长炉宽高云冶1号炉300002543261～40421.55.54云冶2号炉30000231.83310～70022.285.814.5苏力切尔玛3000347～9311.2563.3罗斯卡1200083.3650～4002463今贾5500813120～22013.15.183.0布利赫勒克3000167170～160Φ5（圆形）依玛特拉9000169.1380～1288.58阿纳康达3600012931.78.8茵斯皮雷森51000134.23150～50035.6610.675马弗利拉3600014331.310.364.48杰兹卡兹干500002973600～800247杰兹卡兹干30000178247皮尔多普24000180.53190～38022.164.2 续表12  国内外铜熔炼电炉主要参数（二）厂别炉床面积  m2电极直径  mm电极个数电极电流密度  A/cm2电极中心距离  m云冶1号炉118110064.033云冶2号炉129.5120063.2苏力切尔玛85032.75罗斯卡144120062～33.0今贾68105433布利赫勒克约187803依玛特拉53.266032.45阿纳康达27916506茵斯皮雷森38018006马弗利拉223.5杰兹卡兹干16812006杰兹卡兹干16812006皮尔多普133110063.0 表13  云冶2号30000kVA电炉用变压器技术规格及特征型号电压线高压侧低压侧容量kVA电流，A电压，V电流，AHKDSPZ -10000/351285.7170014286100002285.7168514599100003285.7167014925100004285.7165514267100005285.7164015625100006285.7162516000100007285.7161016395100008285.7159516847100009285.71580173411000010285.71565176991000011285.71550181821000012285.71535186921000013285.71520192311000014285.71505198021000015285.7149020408100001627747520408969417268.5460204089388182604452040891821925143020408877520242415204088470212334002040881632222438520408785723215.537020408755124207355204087245251983402040869362619032520408663327181310204086326     注：该电炉变压器额定功率为50Hz，单相，高压侧电压均为35Kv。 表14  云冶1＃30000kVA电炉炉用变压器技术规格及特性型号电压线高压侧低压侧容量kVA电流，A电压，V电流，AHDPF-10000/351285.7140424780100002285.7138026310100003285.7136027770100004285.7134029410100005285.7132031250100006285.7130033000100007285.7128035700100008285.712613831010000

黄铜带揉捏技术参数的确认    确认黄铜带揉捏技术参数时，能够粽合考虑金属与黄铜带合金制作时的可揉捏性和制品的质量耍求，以满意进步成品率与加工功率的需求。一般是在理论分析的基础上进行各种技术实验，并参阅实践加工经验值来确认合理的技术参数。   A锭坯尺度的挑选   挑选锭坯尺度时应考虑的准则如下:    (1)对锭坯的质贵要求.能够依据揉捏的黄铜带合金、揉捏制品技能要求和加工技术而确认。    (2)为确保揉捏制品端面上的安排和功能均匀，其变形程度大于85%，一般能够取90%以上(即揉捏比大于10),选用大变形程度能够使粗大的晶位破碎而细化，使晶界上的脆性物质转移到晶内，强化了晶教之间的联络，这样能够使揉捏制品有较高的力学功能.大变形程度还能够使揉捏制品的内外层安排均匀.对二次揉捏的坯料能够不受此约束。    (3)在黄铜带揉捏定尺或倍尺产品时，挑选锭坯尺度应该考虑压余厚度的巨细和揉捏制品切头、尾长度所需的金属星。避免呈现制品短尺废品。   (4)为进步成品率，在揉捏机才能答应的条件下.尽量选用长锭坯揉捏，锭坯长度与锭坯直径的挑选应相互配合，一般取锭坯长度为1.5-3倍的锭坯直径。高巴塑性较差的合金.能够选用较短的锭坯。   (5)确认锭坯尺度时，有必要考虑揉捏设备的才能和揉捏工其的强度。在设备才能答应、揉捏东西确保的条件下.尽可能地选用大变形程度揉捏。    (6)核算锭坯直径时，应该归纳考虑揉捏筒直径、锭坯直径和误差量、加热胀大后仍能顺畅进人揉捏筒内等要素。   为了确保操作顺畅进行.揉捏筒与锭坯之间、空心锭坯的内径与穿孔针之间.都应该留有必定的空隙。锭坯与揉捏筒、穿孔针之间的空隙如表4-10所示。    关于塑性很差的合金，在挑选AD时、应选取的小些，以避免充填揉捏时锭坯周边发生裂纹。   实践加工中.锭坯长度的确认还应该考虑切定尺和倍尺的裕最(锯口)。在揉捏管材时，发生的穿孔料头可按实心断面计人，一般穿孔料头的长度为其直径的1一1.5倍。关于不定尺产品.为了进步成品率，很据设备才能和黄铜带揉捏制品规格，能够按厂矿已规格化的常用锭坯来挑选，一般不核算锭坯长度。

1、金属液位 　　金属液位设定是保证铸锭内外部质量的关键参数。金属液位包括初始液位与铸造过程中的液位。初始液位要有利于铸造开始(俗称开头)，它与结晶器填充时间相对应，起到铸造铺底的作用。铸造过程中的液位主要是防止铸造中产生冷隔或拉裂，它与铸造速度，铸造温度及冷却强度相关。同时还要对就考虑金属液位没定高度与液化报警高度的时差，以便达到安全操作与保护设备的目的。 　　2、结晶器填充时间 　　结晶器填充时间也称为液位填充时间，它是计算机进行自动控制的必要工艺参数，液位填充时叫与金属液位高度值形成对应关系。液位填充时间设定相同时，金属液位设定越高，液体注入结晶器的流速越快，结晶器内液体温度越高，在其他条件相同时，冷却速度越慢;反之。液体注入结晶器的流速越慢。结晶器内液体温度越低，冷却速度就越快。 　　金属液位填充高度设定相同时。液位填充时间设定越长，液体注入结晶器的流速越慢，结晶器内液体温度越低，冷却速度越快;反之，液体注入结晶器流速越快，结晶器内液体温度越高，冷却速度越慢。 　　液位填充时间与金属液位高度组合设定的作用是对铸造开车前液体填充速度的控制，即初始铸造速度初始铸造速度对铸造底部温度控制起着关键作用，合适的初始铸造速度可以防止开车后漏铝、拉裂及控制铸锭底部裂纹形态初始铸造速度的设定可依据每个铸次条件的不同设定，比如铸造温度的不同、转注流程温降(包括室温)不同等初始铸造速度是不同的。还可依据牛产合金的特性丛生产规格的不同进行设定。比如裂纹倾向性较大合金与裂纹倾向性较小合金。它们的初始铸造速度是有差别的。

中国输气管道建设的高峰期。石油和天然气作为一种主要能源在国家的经济建设中发挥着越来越重要的作用。随着石油天然气需求量的不断增加 ,管道的输送压力不断增加 ,管线钢管向着大口径、厚壁和高强度方向发展已成趋势。“西气东输”和“陕京二线”天然气输送管线工程就标志着我国采用大口径、厚壁、高压输送管的新起点。为了实现西气东输工程用大口径直缝埋弧焊钢管的国产化 ,巨龙钢管有限公司建成了国内第一条JCOE大口径直缝埋弧焊管生产线 ,直缝钢管是焊缝与钢管纵向平行的钢管。通常分为公制电焊钢管、电焊薄壁管、变压器冷却油管等等。　　生产工艺　　直缝高频焊接钢管具有工艺相对简单，快速连续生产的特点，在民用建筑、石化、轻工等部门有广泛用途。多用于输送低压流体或做成各种工程构件及轻工产品。 　　1.直缝高频焊接钢管的生产工艺流程 　　直缝焊接钢管是通过高频焊接机组将一定的规格的长条形钢带卷成圆管状并将直缝焊接而成钢管。钢管的形状可以是圆形的，也可以是方形或异形的，它取决于焊后的定径轧制。焊接钢管的材料主要是：低碳钢及σs≤300N/mm2、σs≤500N/mm2的低合金钢或其他钢材。直缝钢管高频焊接的生产工艺流程如下： 　　2.高频焊接 　　高频焊接是根据电磁感应原理和交流电荷在导体中的趋肤效应、邻近效应和涡流热效应，使焊缝边缘的钢材局部加热到熔融状态，经滚轮的挤压，使对接焊缝实现晶间接合，从而达到焊缝焊接之目的。高频焊是一种感应焊（或压力接触焊），它无需焊缝填充料，无焊接飞溅，焊接热影响区窄，焊接成型美观，焊接机械性能良好等优点，因此在钢管的生产中受到广泛的应用。 　　钢管的高频焊接正是利用交流电的趋肤效应和邻近效应，钢材（带钢）经滚压成型后，形成一个截面断开的圆形管坯，在管坯内靠近感应线圈中心附近旋转一个或一组阻抗器（磁棒），阻抗器与管坯开口处形成一个电磁感应回路，在趋肤效应和邻近效应的作用下，管坯开口处边缘产生强大而集中的热效应，使焊缝边缘迅速加热到焊接所需温度经压辊挤压后，熔融状态的金属实现晶间接合，冷却后形成一条牢固的对接焊缝。 　　3.高频焊管机组 　　直缝钢管的高频焊接过程是在高频焊管机组中完成的。高频焊管机组通常由滚压成型、高频焊接、挤压、冷却、定径、飞锯切断等部件组成，机组的前端配有储料活套，机组的后端配有钢管翻转机架；电气部分主要有高频发生器、直流励磁发电机和仪表自动控制装置等组成。现以φ165mm高频焊管机组为例，其主要技术参数如下： 　　3.1 焊管成品　　圆管外径： φ111~165mm　　方管： 50×50~125×125mm　　矩形管： 90×50~160×60~180×80mm　　成品管壁厚：2~6mm 　　3.2 成型速度： 20~70米/分钟 　　3.3 高频感应器：　　热功率： 600KW　　输出频率： 200~250KHz　　电源： 三相380V 50Hz　　冷却： 水冷　　激励电压： 750~1500V 　　4.高频激励电路 　　高频激励电路（又称高频振荡电路），是由安装在高频发生器内的大型电子管和振荡槽路组成，它是利用电子管的放大作用，在电子管接通灯丝和阳极时，把阳极输出信号正反馈到栅极，形成自激振荡回路。激励频率的大小取决于振荡槽路的电气参数（电压、电流、电容和电感）。 　　5.直缝钢管高频焊接工艺 　　5.1 焊缝间隙的控制 　　将带钢送入焊管机组，经多道轧辊滚压，带钢逐渐卷起，形成有开口间隙的圆形管坯，调整挤压辊的压下量，使焊缝间隙控制在1~3mm，并使焊口两端齐平。如间隙过大，则造成邻近效应减少，涡流热量不足，焊缝晶间接合不良而产生未熔合或开裂。如间隙过小则造成邻近效应增大，焊接热量过大，造成焊缝烧损；或者焊缝经挤压、滚压后形成深坑，影响焊缝表面质量。 　　5.2 焊接温度控制 　　焊接温度主要受高频涡流热功率的影响，根据公式（2）可知，高频涡流热功率主要受电流频率的影响，涡流热功率与电流激励频率的平方成正比；而电流激励频率又受激励电压、电流和电容、电感的影响。激励频率公式为： 　　f=1/[2π(CL)1/2]...(1)　　式中：f-激励频率(Hz)；C-激励回路中的电容(F)，电容=电量/电压；L-激励回路中的电感，电感=磁通量/电流 　　上式可知，激励频率与激励回路中的电容、电感平方根成反比、或者与电压、电流的平方根成正比，只要改变回路中的电容、电感或电压、电流即可改变激励频率的大小，从而达到控制焊接温度的目的。对于低碳钢，焊接温度控制在1250~1460℃，可满足管壁厚3~5mm焊透要求。另外，焊接温度亦可通过调节焊接速度来实现。 　　当输入热量不足时，被加热的焊缝边缘达不到焊接温度，金属组织仍然保持固态，形成未熔合或未焊透；当输入热时不足时，被加热的焊缝边缘超过焊接温度，产生过烧或熔滴，使焊缝形成熔洞。 　　5.3 挤压力的控制 　　管坯的两个边缘加热到焊接温度后，在挤压辊的挤压下，形成共同的金属晶粒互相渗透、结晶，最终形成牢固的焊缝。若挤压力过小，形成共同晶体的数量就小，焊缝金属强度下降，受力后会产生开裂；如果挤压力过大，将会使熔融状态的金属被挤出焊缝，不但降低了焊缝强度，而且会产生大量的内外毛刺，甚至造成焊接搭缝等缺陷。 　　5.4 高频感应圈位置的调控 　　高频感应圈应尽量接近挤压辊位置。若感应圈距挤压辊较远时，有效加热时间较长，热影响区较宽，焊缝强度下降；反之，焊缝边缘加热不足，挤压后成型不良。 　　5.5 阻抗器是一个或一组焊管专用磁棒，阻抗器的截面积通常应不小于钢管内径截面积的70%，其作用是使感应圈、管坯焊缝边缘与磁棒形成一个电磁感应回路，产生邻近效应，涡流热量集中在管坯焊缝边缘附近，使管坯边缘加热到焊接温度。阻抗器用一根钢丝拖动在管坯内，其中心位置应相对固定在接近挤压辊中心位置。开机时，由于管坯快速运动，阻抗器受管坯内壁的磨擦而损耗较大，需要经常更换。 　　5.6 焊缝经焊接和挤压后会产生焊疤，需要清除。清除方法是在机架上固定刀具，靠焊管的快速运动，将焊疤刮平。焊管内部的毛刺一般不清除。 　　5.7 工艺举例　　现以焊制φ32×2mm 直缝焊管为例，简述其工艺参数：　　带钢规格：2×98mm 带宽按中径展开加少量成型余量　　钢材材质：Q235A　　输入 励磁电压：150V 励磁电流：1.5A 频率：50Hz　　输出 直流电压：11.5kV 直流电流：4A 频率：120000Hz　　焊接速度：50米/分钟　　参数调节：根据焊接线能量的变化及时调节输出电压和焊接速度。参数固定后一般不用调整。 　　6.高频焊管的技术要求与质量检验 　　根据GB3092《低压流体输送用焊接钢管》标准的规定，焊管的公称直径为6~150mm，公称壁厚为2.0~6.0mm，焊管的长度通常为4~10米，可按定尺或倍尺长度出厂。钢管表面质量应光滑，不允许有折叠、裂缝、分层、搭焊等缺陷存在。钢管表面允许有不超过壁厚负偏差的划道、刮伤、焊缝错位、烧伤和结疤等轻微缺陷存在。允许焊缝处壁厚增厚和内缝焊筋存在。 　　焊接钢管应做机械性能试验和压扁试验以及扩口试验，并要达到标准规定的要求。钢管应能承受一定的内压力，必要时进行2.5Mpa压力试验，保持一分钟无渗漏。允许用涡流探伤的方法代替水压试验。涡流探伤按GB7735《钢管涡流探伤检验方法》标准执行。涡流探伤方法是将探头固定在机架上，探伤与焊缝保持3~5mm距离，靠钢管的快速运动对焊缝进行全面的扫查，探伤信号经涡流探伤仪的自动处理和自动分选，达到探伤的目的。 　　探伤后的焊管用飞锯按规定长度切断，经翻转架下线。钢管两端应平头倒角，打印标记，成品管用六角形捆扎包装后出厂。

在水电站压力钢管的焊接一直采用传统、简单而繁重的焊条电弧焊技术，只有少量的制作场纵缝采用埋弧自动焊技术，压力钢管的全位置自动化焊接技术尚属空白。随着水电建设的高速发展和机组参数的不断增大，大直径厚壁压力钢管的焊接必须采用先进的全位置自动化焊接技术才能适应施工生产的需要。 　　压力钢管全位置自动焊不仅要实现焊接小车沿焊缝的自动行走，焊丝的自动输送、凋整，摆动及对中等机电控制过程，而且要解决焊丝的熔滴过渡形式，保证全位置焊接的焊缝成型质量，特别是对各种位置的焊接规范自动调整等一系列自动控制技术；而更重要的是现场拼装的焊缝对装质量差、施工环境恶劣，较难满足自动化焊接施工的要求。目前，压力钢管全位置自动化焊接技术在大直径厚壁压力钢管焊接中全面应用尚有一定难度，其主要原因是： 　　(1)大直径厚壁压力钢管的安装环缝组装难以达到均匀一致的高精度，这就要求全位置自动焊设备能根据坡口尺寸及偏差自动凋整有关工艺参数，以降低或消除不均匀参数对焊接质量的影响； 　　(2)焊缝空间位置不断变化，要求焊接系统能根据焊炬所在位置自动及时调整焊接工艺参数，实现各处焊接成型基本一致； 　　(3)要实现坡口尺寸、焊接熔地形状，焊接规范参数实寸调节三者匹配，保证焊缝质量，其自动控制技术难度较大。 　　因此，如何选择造价低、适应性强、操作简单、焊接效率高的全位置自动化焊接设备是解决上述问题的唯一途径。针对水电站压力钢管的焊接特点，我们开发研制了一套独具特色的全位置自动焊机，并在湖北省兴山县古洞口水电站压力钢管及三峡二期工程左厂11#14#压力钢管纵缝的焊接施工中获得了成功应用。 1 全位置自动焊机的主要研制内容及其实施方案 　　全位置自动焊机研制主要包括机械和电气控制两大部分内容。 1.1 机械设计与制造 　　整机机械设计包括爬行轨道、爬行小车，焊炬摆动机构及摆幅自适应坡口宽度传感器结构设计。 1.1.1 爬行轨道 　　爬行道轨由不锈钢薄板、分体式齿块组成的齿条和固定道轨于工件表面的水磁铁块组成。爬行小车和焊炬摆动的控制拖车分别借助左右共四对滚动轴承对夹持道轨边缘，从而使两者可以沿道轨平稳灵活地移动，借助爬行小车内的行车电机输出轴上的小齿轮与道轨上的齿条啮合并通过两侧联杆使爬行小车与焊炬摆动控制拖车联成一体，使两者可以在道轨上可靠、平稳地运行，实行全位置爬行的功能。 1.1.2 爬行小车 　　爬行小车分主动驱动的行走小车和被动行走的焊炬摆动控制拖车两部分。它们分别在底板下方两侧各有两对互成60°的轴承轮夹紧轨道边缘，运动灵活可靠。夹持轨道的两侧轴承轮中的其中一侧可以通过螺杆和滑块作横向移动以实现小车在轨道上夹持与拆卸，使小车在轨道上装卸十分方便。 1.1.3 焊炬摆动机构 　　焊炬摆动机构是实现焊接电弧横向运动的机构。本系统采用一空心薄壁不锈钢方管。其上固定有条状不锈钢板和齿条作摆杆，摆杆端部安装有焊炬夹紧和传感器固定及调节机构。依靠摆杆上条状不锈钢板两侧有倒角的边缘与安装于立板上的四只轴承外套的V型滚轮相啮合，组成了摆动十分灵活、轻巧、刚度好、间隙小、工作稳定可靠、拆卸十分方便的摆动机构。 1.1.4 摆幅自适应坡口宽度和焊接自动跟踪两用传感器 　　摆幅和跟踪两用传感器是为了适应在水电站现场施工条件下，大直径厚壁压力钢管的环缝坡口装配很难做到间隙均匀，而且全位置自动化焊接时轨道的铺设也很难与焊缝完全平行而设计的。本机传感器采用探针机械接触坡口侧壁获取信号，这是一种工作可靠、抗干扰能力最强的获取信号方式，然后通过传感器内部的摆杆系统产生光电信号，经逻辑电路分辨控制焊炬摆动电机转向和停留，实现了焊炬摆幅自适应坡口宽度的功能。 1.2 电气控制系统研制 　　焊机电气控制系统设计功能的完善、工作稳定可靠、抗干扰性好对于确保焊机工作质量十分重要。本焊机充分考虑了全位置自动化焊机所必须的基本功能和参考国内外同样先进焊机的功能，开发了具有自身特点的摆幅自适应坡口宽度和自动跟踪焊接控制功能。本机具备的主要控制功能如下： 　　1)焊炬摆幅自动与手动选择； 　　2)焊炬摆幅设定与自适应选择； 　　3)焊炬摆动两侧停留时间调节； 　　4)焊炬摆速调节； 　　5)焊接电弧运动轨迹选择； 　　6)焊接方向选择； 　　7)焊接速度凋节； 　　8)设定摆幅工作方式下始摆方向选择； 　　9)设定摆幅工作方式下电弧纠偏调节； 　 10)焊接行车小车近控与遥控。 　　其电气控制原理如下图所示： 2 整机主要技术参数： 小车电源： 　　　220V 50HZ 小车爬行速度 　　0～450mm/min 焊炬摆动幅度 　　0～±40mm 焊炬摆动速度 　　250～3000mm/min 焊炬摆动方式 　　1)直线形；2)锯齿形；3)梯形；4)矩形 焊炬两侧停留时间　 0～5sec 自动跟踪精度 　　±0.5sec 焊炬调整自由度 　6个 焊接钢管曲率半径 ≥1500mm 焊机重量　　　　 18.5 kg 　　本焊机适应的焊接方法不受限制，可以根据需要采用CQ2气体保护焊、药芯焊丝气保焊、药芯焊丝自保焊、MAG焊、MIG焊、TIG焊等方法，只需配以相应特性的焊接电源和焊炬。 3 工程应用与效果 3.1 应用工程简介 　　古洞口水电站位于湖北省兴山县古夫河下游，电站总装机容量为4.5万kW，多年平均发电量为1.24亿kwh，其压力钢管直径为5m，壁厚为16～40mm不等，全长600余m。全部采用国产16Mn低合金结构钢制造。 　　三峡工程是举世瞩目的水电工程，其装机总容量为1 820万kW，年发电量达847亿kwh，其压力钢管直径为12.4m，壁厚为26～541mm，单管长度122.5m，采用国产16MnR低合金结构钢和进口600MPa级低碳调质高强钢板制造。 3.2 全位置自动焊工艺 　　全位置自动焊工艺参数见表1。 表1 全位置自动焊工艺参数表 3.3 应用效果 　　(1)全位置自动焊与传统焊条电弧焊的各项性能效果对比如表2： 表2 全位置自动焊应用效果对比表 　　(2)通过对古洞口压力钢管和三峡二期工程左厂11#～14＃压力钢管的焊接应用，纵缝超声波探伤的一次合格率为99.5％，环缝超声波探伤的一次合格率达98.1%，焊缝外观质量优良率达到了100％，这是传统的焊条电弧焊所无法比拟的。 　　(3)该焊接小车采用柔性轨道，机头行走摆动、焊缝两侧停留均能做到无级调速、自动送丝，稳定可靠，达到了全位置自动化焊接的基本要求。 　　(4)由于实现了机械化和自动化的焊接新技术，不仅减轻了焊工的劳动强度，而且大大提高了焊缝无损探伤的一次合格率，在焊接质量上大大减少了人为因素的影响。 　　(5)采用连续送丝和大电流密度焊接，与焊条电弧焊相比可提高工效1倍以上。 　　(6)与焊条电弧焊相比，该自动焊工艺具有较深的熔深，可采用较小坡口角度，同时可以大大降低焊接热影响区的宽度和焊接残余变形。 4 结束语 　　全位置自动焊机在吸取了国外同类焊机成功经验的基础上针对水电站压力钢管现场施工特点，创造性的开发；厂焊炬摆幅自适应坡口宽度和自动跟踪等重要功能，焊机整体设计合理，工作稳定可靠、外形美观、机构紧凑轻便，具有很高的推广应用价值。 　　全位置自动化焊接技术在古洞口压力钢管纵环缝及三峡二期工程左厂11#～14#压力钢管纵缝焊接施工中的成功应用，只是自动化焊接技术在水电站焊接施工中应用的一个开端，该设备与技术在三峡工程压力钢管环缝焊接中应用将是我们下一步追求的目标。全位置自动焊在水电站压力钢管及蜗壳上的应用也是焊接施工技术发展的必然结果

国标无缝钢管是用钢锭或实心管坯经穿孔制成毛管，然后经热轧、冷轧或冷拨制成。在我国钢管业中具有重要的地位，分热轧和冷轧（拨）无缝钢管两类。尺寸及允许偏差： D1 ±1.5%，最小±0.75 mmD2 ±1.0%。最小±0.50 mmD3 ±0.75%．最小±0.30 mmD4 ±0.50%。最小±0.10 mm 国标无缝钢管重量公式： 　　[(外径-壁厚)*壁厚]*0.02466=kg/米（每米的重量） 无缝钢管的国标是GB8162、直缝焊接钢管的国标是GB/T13793， 　　GB8162无缝钢管　GB8162无缝钢管与GB8163的区别 GB8162《结构用无缝钢管》，此标准适用于一般结构、机械结构用无缝钢管，GB8163《输GB8162送流体用无缝钢管》标准适用于输送流体的一般无缝钢管。它与GB8162的主要区别是GB8163钢管逐根进行液压试验或进行超声波、涡流、漏磁探伤。因此，在压力管道钢管的标准选用上，不宜采用GB8162标准。钢管品种钢管标准常用钢管牌号常用国外钢管标准结构用无缝钢管GB/T8162-199910、20、35、45、40Mn2、45Mn2、27SiMn、20Cr、40Cr、20CrMo、35CrMo、38CrMoA1、30CrMnSi、50CrV、ASTM A500-98ASTM A501-98、ASTN A519-98、JIS G3441-1994 输送流体用无缝钢管  GB/T8163-199910、20、Q295、Q345ASTM A53-98、ASTM A192、ASME S192、JIS G3452-1998、FIS G3454-1998、DIN 1629-1984油井用油管、接箍料管管线钢管API SPEC 5CTAPE SPEC 5LJ55、N80 A、B、X42API高压锅炉用无缝钢管GB5310-199520G、20MnG、25MnG、15MoG、20MoG、12Cr1MoVG、15CrMoVG、12Cr2MoG、12Cr2MoWVTiB、12Cr3MoVSiTiBASTM A106-96a、ATSMA213-95a、JISG3461-1988、JISG3462-1998、DIN 17175-1979、BS3059：Part 2：1990低中压锅炉用无缝钢管GB3087-199910、20ASTM A179、ASTM A192、BS3059化肥设备用高压无缝钢管GB6479-8610、20G、Q345、Q390、10MoVNb、12CrMo、15CrMo、12Cr2MoISO 9329-2-1997、ASTM A161-94石油裂化用无缝钢管GB9948-8610、20、12CrMo、15CrMo、1Cr2Mo、1Cr5MoJIS G3441-1988汽车半轴套管用无缝钢管Q/OHAD001-1997YB/T5035-199845Mn2、45、25MnCrDIN 1629-1984液压支柱用热轧无缝钢管Q/OHAD010-1998GB/T17398-199827SiMn 船舶用碳钢、碳锰钢无缝钢管GB/T5312-1999Q320、Q360、Q410、Q460、Q490DIN 2391-1994冷拔精密无缝钢管GB/T3639-83GB/T8713-8810、20、35、45、20CrMo 地质钻探用无缝钢管YB/T5052-93YB235-70DZ40、DZ50 炮弹用无缝钢管YBn1-8640Mn2、D60 顶杆用无缝钢管Q/OHAD003-941CrMo 轴承钢管YB/Z12-77YJZ84GCr15 带肋钢筋连接套筒用无缝钢管Q/OHAD011-1997a10、20 气瓶用无缝钢管技术协议34Mn2V、30CrMo、35CrMo、45 进口无缝钢管和国产无缝钢管的差距在于价格，目前国内无缝钢管制造水平也是比较高的，像天钢，冶钢，宝钢，中钢联，汇通制造钢管已达国际先进水平。

无缝钢管无缝钢管是用实心管坯经穿孔后轧制的。1、生产制造方法按生产方法不同可分为热轧管、冷轧管、冷拔管、挤压管等。1.1、热轧无缝管一般在自动轧管机组上生产。实心管坯经检查并清除表面缺陷，截成所需长度，在管坯穿孔端端面上定心，然后送往加热炉加热，在穿孔机上穿孔。在穿孔同时不断旋转和前进，在轧辊和顶头的作用下，管坯内部逐渐形成空腔，称毛管。再送至自动轧管机上继续轧制。最后经均整机均整壁厚，经定径机定径，达到规格要求。利用连续式轧管机组生产热轧无缝钢管是较先进的方法。 1.2、若欲获得尺寸更小和质量更好的无缝管，必须采用冷轧、冷拔或者两者联合的方法。冷轧通常在二辊式轧机上进行，钢管在变断面圆孔槽和不动的锥形顶头所组成的环形孔型中轧制。冷拔通常在0.5～100T的单链式或双链式冷拔机上进行。 1.3、挤压法即将加热好的管坯放在密闭的挤压圆筒内，穿孔棒与挤压杆一起运动，使挤压件从较小的模孔中挤出。此法可生产直径较小的钢管。 2、用途 2.1、无缝管用途很广泛。一般用途的无缝管由普通碳素结构钢、低合金结构钢或合金结构钢轧制，产量最多，主要用作输送流体的管道或结构零件。 2.2、根据用途不同分三类供应：a、按化学成分和机械性能供应；b、按机械性能供应；c、按水压试验供应。按a、b类供应的钢管，如用于承受液体压力，也要进行水压试验。 2.3、专门用途的无缝管有锅炉用无缝管、地质用无缝管及石油用无缝管等多种。 3、种类 3.1、无缝钢管按生产方法不同可分为热轧管、冷轧管、冷拔管、挤压管等。 3.2、按外形分类有圆形管、异形管之分。异形管除方形管和矩形管外，还有椭圆管、半圆管、三角形管、六角形管、凸字形管、梅花形管等。 3.3、按材质的不同，分为普通碳素结构管、低合金结构管、优质碳素结构管、合金结构管、不锈管等。 3.4、按专门用途分，有锅炉管、地质管、石油管等。 4、规格及外观质量 无缝管按GB/T8162-87规定 4.1、规格：热轧管外径32～630mm。壁厚2.5～75mm。冷轧(冷拔)管外径5～200mm。壁厚2.5～12mm。 4.2、外观质量：钢管的内外表面不得有裂缝、折叠、轧折、离层、发纹和结疤缺陷存在。这些缺陷应完全清除掉，清除后不得使壁厚和外径超过负偏差。 4.3、钢管的两端应切成直角，并清除毛刺。壁厚大于20mm的钢管允许气割和热锯切割。经供需双方协议也可不切头。 4.4、冷拔或冷轧精密无缝钢管《表面质量》参照GB3639-83。 5、化学成分检验 5.1、按化学成分和机械性能供应的国产无缝管，如10、15、20、25、30、35、40、45和50号钢的化学成分应符合GB/T699-88的规定。进口无缝管按合同规定的有关标准检验。09MnV、16Mn、15MnV钢的化学成分应符合GB1591-79的规定。 5.2、具体分析方法参照GB223-84《钢铁及合金化学分析方法》的有关部分。 5.3、分析偏差参照GB222-84《钢的化学分析用试样及成品化学成分允许偏差》。 6、物理性能检验 6.1、按机构性能供应的国产无缝管，普通碳素钢按GB/T700-88的甲类钢制造(但必须保证含硫量不超过0.050%和含磷量不超过0.045%)，其机械性能应符合GB8162-87表内所规定的数值。 6.2、按水压试验供应的国产无缝管必须保证标准所规定的水压试验。 6.3、进口无缝管的物理性能检验按合同规定的有关标准进行。 7、主要进出口情况 7.1、一般无缝管进口量很大。主要进口国家是德国和日本。欧洲国家如罗马尼亚、俄罗斯、瑞士、法国、西班牙、捷克、南斯拉夫、匈牙利等国都有进口。还有少量从南美的阿根廷、墨西哥等国进口。 7.2、根据我国用货单位的不同要求，进口无缝管规格多达100多种，常见的规格有15922mm、1595mm、15918mm。114.38mm、114.310mm、114.313mm。长度一般为5～8m或4～7m不等。主要是热轧碳结构，钢号为ST35.ST45及ST65。进口规格直径最小的为305mm，最大的47813mm。 7.3、从法国和西班牙曾进口少量直径较小而壁薄的无缝管，如183mm，223mm、26.93mm等。执行德国曼内斯曼钢管厂的一般规则。 7.4、从匈牙利和日本进口的无缝管，常参照DIN2448、DIN1629。 7.5、在进口索赔案例中，进口无缝管存在的质量问题主要有：化学成分不合格、压扁试验发生劈裂、抗拉强度低、出现严重锈蚀及凹坑等。 8、包装 按GB2102-88规定。钢管包装分三种：捆扎、装箱、涂油捆扎或涂油装箱。

1、电压　　电泳涂装采用的是定电压法，设备相对简单，易于控制。电压对漆膜的影响很大；电压越高，电泳漆膜越厚，对于难以涂装的部位可相应提高涂装能力，缩短施工时间。但电压过高，会引起漆膜表面粗糙，烘干后易产生“橘皮”现象。电压过低，电解反应慢，漆膜薄而均匀，泳透力差。电压的选择由涂料种类和施工要求等确定。一般情况下，电压与涂料的固体分及漆温成反比，与两极间距成正比。钢铁表面为40～70V，铝和铝合金表面可采用60～100V，镀锌件采用70～85V。　　2、电泳时间　　漆膜厚度随着电泳时间的延长而增加，但当漆膜达到一定厚度时，继续延长时间，也不能增加厚度，反而会加剧副反应；反之，电泳时间过短，涂层过薄。电泳时间应根据所用的电压，在保证涂层质量的条件下，越短越好。一般工件电泳时间为1至3分钟，大型工件为3至4分钟。如果被涂物件表面几何形状复杂，可适当提高电压和延长时间。　　3、涂料温度　　涂料温度高，成膜速率快，但漆膜外观粗糙，还会引起涂料变质；温度低，电沉积量少，成膜慢，涂膜薄而致密。施工过程中，由于电沉积时部分电能转化成热能，循环系统内机械摩擦产生热量，将导致涂料温度上升。一般漆液温度控制在某些方面15～30℃。　　4、涂料的固体分和颜基比　　市售的电泳涂料的固体分一般为50%左右，施工时，需用蒸馏水将涂料固体分控制在10%～15%。固体含量太低，漆膜的遮盖力不好，颜料易沉淀，涂料的稳定性差。固体分过高，粘度提高，会造成漆膜粗糙疏松，附着力差。一般颜基比为1比2左右，高光泽电泳涂料的颜基比可控制在1比4。由于实际操作中，涂料的颜料量会逐渐下降，必须随时添加颜料分高的涂料来调节。　　5、涂料的PH值　　电泳涂料的PH值直接影响槽液的稳定性。PH值过高，新沉积的涂膜会再溶解，漆膜变薄，电泳后冲洗会脱膜。PH值过低，工件表面光泽不一致，漆液的稳定性不好，已溶解的树脂会析出，漆膜表面粗糙，附着力降低。一般要求施工过程中，PH值控制在7.5～8.5之间。在施工工程中，由于连续进行电泳，阳离子的铵化合物在涂料中积蓄，导致PH值的上升。可采用补加低PH值的原液，更换阴极罩蒸馏水，用离子交换树脂除去铵离子，采用阳极罩等方法降低PH值。若PH值过低时，可加入乙醇铵来调节。　　6、涂料电阻　　被涂物件从前一道工序带入电泳槽的杂质离子等引起涂料电阻值的下降，从而导致漆膜出现粗糙不均和针孔等弊病。在涂装施工中，需对涂料进行净化处理。为了得到高质量涂膜，可采用阴极罩设备，以除去铵及钙、镁等杂质正离子。　　7、工件与阴极间距离　　距离近，沉积效率高。但距离过近，会使漆膜太厚而产生流挂、橘皮等弊病。一般距离不低于500px。对大型而形状复杂的工件，当出现外部已沉积很厚涂膜，而内部涂膜仍较薄时，应在距离阴极较远的部位，增加辅助阴极。

性能指标 AM-70 AM-85 AM-92 中档AL2O3% 71-77 81-86 88-92 52-60MgO% 22-27 13-17 7-11 37-47SiO2% ≤0.3 ≤0.3 ＜0.25 ＜2.5CaO% ≤0.4 ≤0.3 ＜0.2 TiO2＜3Na2O% ≤0.3 ≤0.4 ＜ —Fe2O3% ≤0.3 ≤0.3 ＜0.3 ＜2体积密度 ≥3.35 ≥3.40 ≥3.45　　　　 —真密度 ≥3.35 ≥3.53 ≥3.56 —显气孔率 ＜3.5 ＜4.0 ＜5.0 —矿物相组成 尖晶石 尖晶石、微量刚玉a 尖晶石、刚玉 尖晶石、方镶石粒度 8-5MM 5-3MM 3-1MM 1-0MM细粉 180F 200F 240F 325F

疏浚钢管是主要用于清理输送泥沙，泥浆以及其它混合杂物的钢制管道。主要为螺旋钢管，无缝钢管和直缝钢管。疏浚钢管广泛应用于海滩，河道，航道，城市环保，工程施工等领域。天津滨海腾飞钢铁有限公司地处天津北辰区南仓道储宝市场，公司主营国产进口高温高压锅炉管、合金钢锅炉管，规格齐全，高压合金管，石油裂化管，液压支架管，化肥专用管，高压锅炉管，液压支柱管，16Mn钢管，无缝管（16Mn无缝管、27SiMn无缝管）、圆钢（Q345B圆钢、16Mn圆钢）并为电厂及锅炉电站进口整套锅炉管道材料。疏浚钢管

国标钢管规格产品类别国标钢管规格主要材质国标钢管规格执行标准国标钢管规格用途国标钢管规格规格范围高压锅炉管20G、A106cST45.8/3GB5310-95ASTMA106-99DIN17175-79高压锅炉用耐热无缝钢管∮16-824×2-65  　合金管12Cr1MoVP22(10CrMo910)T91、P91、P9、T9 WB36、Cr5Mo(P5、STFA25、T5、)15CrMo(P11、P12、STFA22)13CrMo44、Cr5Mo、15CrMo、25CrMo、30CrMo、40CrMo DIN17175-79JISG3467-88JISG3458-88 　 GB5310-95 GB9948-88ASTMA335/A335mASTMA213/A213m石油、化工、电力、锅炉行业的耐高温、耐低温、耐腐蚀用无缝钢管∮16-824×2-100 不锈钢301 302 304 304L 304H 305 316 316L 316Ti 317 317L 310S 321 321H 347HGB/T14976-2002 GB13296-91 GB5310-95 GB6479-2000 GB9948-88 ASTM312 ASTM213不锈钢高压无缝钢管 1Cr18Ni9TiФ6-680×0.5-40 高压合金无缝钢管T91/P91、P92、15CrMoG、12Cr1MoVGGB3087-99 GB5310-95  GB6479-2000 石油、化工、电力、锅炉行业的耐高温、耐低温、耐腐蚀用无缝钢管∮60-830×0.53-60 石油套管J55　　N80API  SPEC  5CT油井用油管、接箍料管∮60-630×1.53-40 低中压锅炉管10、20GB3087-1999低中压锅炉过热用管、 沸水管、机车大小烟管∮10-530×2-40 石油裂化管2012CrMo15CrMoGB9948-88石油炼精厂的炉管、热交换管、管道用无缝管∮10.530×1.5-36 化肥设备用高压无缝管20、16Mn、Q345GB6479-2000化肥设备、管道∮25-426×6-40 液压支柱管27SiMnGB/T17396-1998液压支架液压支柱∮70-377×9-40 船用管410GB/T5312-1999制造船舶专用耐压管、锅炉及过热器用管∮14-426*1.5-4.5 管线管B级API石油、天然气 工业输送气、水、油∮60-630×1.53-40 流体管20、Q345GB/T8163-1999流体输送∮8-630×1.5-40 结构管10、20、35、45、16Mn? Q345BGB/T8162-1999一般结构用∮6-610×1.5-40 精密管St35 St37.4(10#) St45(20#)St55(35#) Ck45(45#)St52(16Mn) CH8Ni9Ti 35CroGB/T3639-2000DIN2391用于汽车、摩托车、工程机械、千斤顶、电动工具及运动器材等其他领域所用的精密钢管∮4-89

钢管表面处理是钢管的使用寿命的关键因素之一，它是防腐层与钢管能否牢固结合的前提。经研究机构验证，防腐层的寿命除取决于涂层种类、涂覆质量和施工环境等因素外，钢管的表面处理对防腐层寿命的影响约占50％，因此，应严格按照防腐层规范对钢管表面的要求，不断探索和总结，不断改进钢管表面处理方法。     1、清洗     利用溶剂、乳剂清洗钢材表面，以达到去除油、油脂、灰尘、润滑剂和类似的有机物，但它不能去除钢材表面的锈、氧化皮、焊药等，因此在防腐生产中只作为辅助手段。       2、工具除锈     主要使用钢丝刷等工具对钢材表面进行打磨，可以去除松动或翘起的氧化皮、铁锈、焊渣等。手动工具除锈能达到Sa2级，动力工具除锈可达到Sa3级，若钢材表面附着牢固的氧化铁皮，工具除锈效果不理想，达不到防腐施工要求的锚纹深度。（ 中国喷砂机网 www.penshaji.com ）     3、酸洗     一般用化学和电解两种方法做酸洗处理，管道防腐只采用化学酸洗，可以去除氧化皮、铁锈、旧涂层，有时可用其作为喷砂除锈后的再处理。化学清洗虽然能使表面达到一定的清洁度和粗糙度，但其锚纹浅，而且易对环境造成污染。     4、喷(抛)射除锈     喷(抛)射除锈是通过大功率电机带动喷(抛)射叶片高速旋转，使钢砂、钢丸、铁丝段、矿物质等磨料在离心力作用下对钢管表面进行喷(抛)射处理，不仅可以彻底清除铁锈、氧化物和污物，而且钢管在磨料猛烈冲击和磨擦力的作用下，还能达到所需要的均匀粗糙度。 　　喷(抛)射除锈后，不仅可以扩大管子表面的物理吸附作用，而且可以增强防腐层与管子表面的机械黏附作用。因此，喷(抛)射除锈是管道防腐的理想除锈方式。一般而言，喷丸(砂)除锈主要用于管子内表面处理，抛丸(砂)除锈主要用于管子外表面处理。采用喷(抛)射除锈应注意几个问题。     4．1除锈等级     对于钢管常用的环氧类、乙烯类、酚醛类等防腐涂料的施工工艺，一般要求钢管表面达到近白级(Sa2．5)。实践证明，采用这种除锈等级几乎可以除掉所有的氧化皮、锈和其他污物，锚纹深度达到40~100μm，充分满足防腐层与钢管的附着力要求，而喷(抛)射除锈工艺可用较低的运行费用和稳定可靠的质量达到近白级(Sa2．5)技术条件。     4．2喷(抛)射磨料     为了达到理想的除锈效果，应根据钢管表面的硬度、原始锈蚀程度、要求的表面粗糙度、涂层类型等来选择磨料，对于单层环氧、二层或三层聚乙烯涂层，采用钢砂和钢丸的混合磨料更易达到理想的除锈效果。钢丸有强化钢表面的作用，而钢砂则有刻蚀钢表面的作用。钢砂和钢丸的混合磨料(通常钢丸的硬度为40～50 HRC，钢砂的硬度为50～60 HRC可用于各种钢表面，即使是用在C级和D级锈蚀的钢表面上，除锈效果也很好。     4．3磨料的粒径及配比     为获得较好的均匀清洁度和粗糙度分布，磨料的粒径及配比设计相当重要。粗糙度太大易造成防腐层在锚纹尖峰处变薄；同时由于锚纹太深，在防腐过程中防腐层易形成气泡，严重影响防腐层的性能。      粗糙度太小会造成防腐层附着力及耐冲击强度下降。对于严重的内部点蚀，不能仅靠大颗粒磨料高强度冲击，还必须靠小颗粒打磨掉腐蚀产物来达到清理效果，同时合理的配比设计不仅可减缓磨料对管道及喷嘴(叶片)的磨损，而且磨料的利用率也可大大提高。通常，钢丸的粒径为0.8～1.3 mm，钢砂粒径为0.4～1.0 mm，其中以0.5～1.0 mm为主要成分。砂丸比一般为5～8。     应该注意的是在实际操作中，磨料中钢砂和钢丸的理想比例很难达到，原因是硬而易碎的钢砂比钢丸的破碎率高。为此，在操作中应不断抽样检测混合磨料，根据粒径分布情况，向除锈机中掺入新磨料，而且掺人的新磨料中，钢砂的数量要占主要的。     4．4除锈速度 钢管的除锈速度取决于磨料的类型和磨料的排量，即单位时间内磨料施加到钢管的总动能E及单颗粒磨料的动能E1。     式中： m ——磨料的喷(抛)量；     　　　 V ——磨料运行速度；    　　　  m1——单颗粒磨料的质量。     m。的大小与磨料破碎率有关，破碎率大小直接影响表面处理作业的成本及除锈设备的费用。当设备固定不变后，m为常数，y为常数，所以E也是一个常数，但由于磨料破碎，m1发生变化，因此，一般应选择损耗率较低的磨料，这样有利于提高清理速度和长叶片的寿命。     4．5清洗和预热     在喷(抛)射处理前，采用清洗的方法除去钢管表面的油脂和积垢，采用加热炉对管体预热至40一60℃，使钢管表面保持干燥状态。在喷(抛)射处理时，由于钢管表面不含油脂等污垢，可增强除锈的效果，干燥的钢管表面也有利于钢丸、钢砂与锈和氧化皮的分离，使除锈后的钢管表面更加洁净。     5 结语     在生产中重视表面处理的重要性，严格控制除锈时的工艺参数，在实际施工中，钢管防腐层的剥离强度值大大超过标准的要求，确保了防腐层的质量，在同样设备的基础上，大大提高工艺水平，降低生产成本。