钢种力学性能化学成份屈从强度 抗拉强度 伸长率 C Si Mn S PMPa kg/mm² MPa kg/mm² min 不大于 不大于 不大于Q215A Q215B  215 22 335-410 34-42 31 0.09-0.15 0.03 0.25-0.55 0.050 0.045  0.045Q235A Q235BQ235CQ235D  235 24 375-460 38-47 26 0.14-0.22 0.12-0.20≤0.18≤0.17  0.30 0.30-0.65 0.30-0.700.35-0.800.35-0.80  0.50 0.450.400.035  0.045 0.0450.0400.035 16Mn(Q345B) 345 35 510-600 51.60 22 0.12-0.20 0.20-0.55 1.2-1.6 0.045 0.045X42 289 29.5 413 42.1 　 0.28 - 1.25 0.030 0.030X52 358 36.5 455 46.4 0.30 - 1.35 0.030 0.030X56 386 39.4 489 49.9 0.26 - 1.35 0.030 0.030X60 413 42.1 517 52.7 0.26 - 1.35 0.030 0.030X65 448 45.7 530 54.0 0.26 - 1.40 0.030 0.030X70 482 49.2 565 57.6 0.26 - 1.40 0.030 0.030L245 245 　 415 　 21 0.26 　 1.15 0.030 0.030L290 290 　 415 　 21 0.28 　 1.25 0.030 0.030L360 360 　 460 　 19 0.3 　 1.25 0.030 0.030

Q235钢板化学成分Q235钢板牌号Q235钢板等级Q235钢板化学成分（质量分数）（%）CMnSiSP≤  Q235A0.14~0.220.30~0.65  0.300.0500.045B0.12~0.200.30~0.700.045C≤0.180.35~0.800.0400.040D≤0.170.0350.035 Q235钢板力学性能Q235钢板牌号拉力强度MPa屈服点MPa伸长率（%）Q235375~50023526

Q235是普通碳素结构钢－普板是一种钢材的材质。Q代表的是这种材质的屈服度，后面的235，就是指这种材质的屈服值，在235MPa左右。并会随着材质的厚度的增加而使其屈服值减小。由于含碳适中，综合性能较好，强度、塑性和焊接等性能得到较好配合，用途最广泛。 由Q+数字+质量等级符号+脱氧方法符号组成。它的钢号冠以“Q”，代表钢材的屈服点，后面的数字表示屈服点数值，单位是MPa例如Q235表示屈服点（σs）为235 MPa的碳素结构钢。 　　②必要时钢号后面可标出表示质量等级和脱氧方法的符号。质量等级符号分别为A、B、C、D。脱氧方法符号：F表示沸腾钢；b表示半镇静钢：Z表示镇静钢；TZ表示特殊镇静钢，镇静钢可不标符号，即Z和TZ都可不标。例如Q235-AF表示A级沸腾钢。 　　③专门用途的碳素钢，例如桥梁钢、船用钢等，基本上采用碳素结构钢的表示方法，但在钢号最后附加表示用途的字母。 化学成分： Q235分A、B、C、D四级(GB/T 700-2006) 　　Q235A级含 C ≤0.22% Mn ≤1.4% Si ≤0.35% S ≤0.050 P ≤0.045 　　Q235B级含 C ≤0.20% Mn ≤1.4% Si ≤0.35% S ≤0.045 P ≤0.045 　　Q235C级含 C ≤0.17% Mn ≤1.4% Si ≤0.35% S ≤0.040 P ≤0.040 　　Q235D级含 C ≤0.17% Mn ≤1.4% Si ≤0.35% S ≤0.035 P ≤0.035 　Q235钢管是碳素结构钢（GB/700-1999）,Q235钢管规格此类钢一般由转炉或平炉冶炼，其主要原料为铁水加废钢，钢中硫、磷含量高于优质碳素结构钢，一般硫≤0.050%，磷≤0.045%。由原料带入钢中的其他合金元素含量，如铬、镍、铜一般不超过0.30%，按成分和性能要求，此类钢的牌号由Q195，Q215A、B，Q235A、B、C、D，Q255A、B，Q275等钢级表示。 　　注：“Q”是屈服的“屈”字的汉语拼音大写字头，其后数字为该牌号最小屈服点（σs）值，其后的符号是按照该钢杂质元素（硫、磷）含量由高到低并伴随碳、锰元素的变化而分为A、B、C、D四等。 　　Q235钢管规格钢产量最大，用途很广，多轧制成板材、型材（圆、方、扁、工、槽、角等）及异型材以及制造焊接钢管。主要用于厂房、桥梁、船舶等建筑结构和一般输送流体用管道。此类钢一般不经热处理直接使用。 　　Q235钢管用来输送低压流体。一般焊管用Q195A、Q215A、Q235A钢制造。也可采用易于焊接的其它软钢制造。钢管要进行水压、弯曲、压扁等实验，对表面质量有一定要求，通常交货长度为4-10m，常要求定尺（或倍尺）交货。焊管的规格用公称口径表示（毫米或英寸）公称口径与实际不同，焊管按规定壁厚有普通钢管和加厚钢管两种，钢管按管端形式又分带螺纹和不带螺纹两种。

q345b钢管化学成分及力学性能和工艺性能   Q345B钢管是无缝钢管的其中一种材质。Q代表的是这种材质的屈服，后面的345就是指这种材质的屈服值，在345左右，并会随着材质的厚度的增加而使其屈服值减小。 Q345B级，是20度常温冲击,这是等级的区分，所代表的，主要是冲击的温度有所不同。   钢管市场上竞争力，扩大企业产品范围，工艺技术室就公司炼钢、轧钢生产工艺及装备的现状，并结合炼钢、轧钢生产实际和低合金钢HRB335的化学成份、力学性能的数据统计及外厂生产q345b化学成分的经验，对开发新品种—低合金高强度结构钢（q345b化学成分）进行充分研究，目前现有装备及生产操作水平条件下，开发新产品低合金高强度结构钢（q345b化学成分）是可行的。 一、q345b化学成分产品标准 执行标准GB/T1591—94《低合金高强度结构钢》 二、q345b化学成分的适应范围 适用于热轧、控轧、正火、正火加回火及淬火状态供应的工程用钢和一般结构用厚度不小于3mm的钢板、钢带及型钢、钢棒。 三、q345b化学成分的化学成分及力学性能和工艺性能 表一是q345b化学成分钢标准要求的化学成分(熔炼成分) 表二是标准规定的q345b化学成分钢材力学、工艺性能值 3.3尺寸、外形、重量等要求 尺寸、外形、重量允许偏差及表面质量应符合相关规定，对于我公司而言，用q345b化学成分钢坯生产建筑用圆钢，其钢材的外形尺寸及表面质量等应符合GB13013《钢筋混凝土用热轧光圆钢筋》的相应规定。 四、钢管冶炼工艺 q345b化学成分级钢的冶炼方法与HRB335相同。均可采用相同的合金化工艺技术，来增加钢中合金元素[si]、[Mn]含量，使其含量达到标准的要求。 五、钢管轧制工艺 q345b化学成分钢可通过加热工艺后进行轧制，其轧制工艺与生产热轧圆钢相同，能保证钢材的力学、工艺性能、外形尺寸、重量、表面质量等。 六、q345b化学成分与HRB335的对比 表三是q345b化学成分的化学成分、力学性能与HRB335的化学成分、力学性能对比表，从表中可以看出这两钢种的化学成分和力学性能相近，根据我室对生产HRB335的熔炼成分和力学、工艺性能数据统计，只要在目前生产HRB335的基础上将熔炼成分进行适当调整，生产q345b化学成分钢材的化学成分和力学、工艺性能是完全能达到标准的要求。

16Mn低合金钢管材质：16Mn，Q345B材质：16Mn，Q345B材质：16Mn，Q345B材质：16Mn，Q345B规格 材质规格 材质规格 材质规格 材质22*2.5 16Mn89*6 Q345B133*7 Q345B245*12 Q345B25*2.5 16Mn89*6 Q345B133*7 16Mn273*8 Q34525*4.5 16Mn89*6.5 16Mn133*8 Q345B273*10 Q34532*3 16Mn89*7 Q345B133*9 Q345B273*10 Q345B42*4 16Mn89*7 16Mn133*10 Q345B273*12 Q345B45*3 Q345B89*8 16Mn133*10 16Mn273*14 Q345B45*4 16Mn89*10 16Mn140*6 Q345B299*8 Q345B50*4 16Mn89*12 Q345B140*8 Q345B299*10 Q34550*5 Q345B89*13 Q345B146*8 Q345B299*12 Q345B51*4.5 16Mn95*4 Q345B159*6 Q345B299*16 Q345B57*3.5 Q345B95*5 Q345B159*10 Q345B325*8.5 Q34557*4 16Mn95*5.5 Q345B159*12 Q345B325*12 Q345B57*5 16Mn95*8 Q345B168*6 Q345325*14 Q345B60*3 16Mn102*5.5 Q345B168*7 Q345325*16 Q345B60*3.2 16Mn102*6 Q345B168*8 Q345351*9 Q345B60*5 Q345B102*7 Q345B168*8 Q345B351*10 Q345B63.5*5 16Mn102*14 16Mn168*10 Q345B351*14 Q34565*4 16Mn102*16 16Mn168*12 Q345B351*14 Q34567*5.5 16Mn108*4 16Mn180*6 Q345B351*16 Q345B68*3 16Mn108*5 16Mn180*8 Q345356*8 Q34570*5 Q345B108*7 16Mn180*8 Q345B377*14 Q345B70*7 16Mn108*8 16Mn180*10 Q345B402*9 Q345B73*3.5 16Mn108*13 16Mn180*12 Q345B402*10 Q345B73*5 Q345B114*4 16Mn180*16 Q345B402*12 Q345B73*6.5 16Mn114*5 Q345B194*6 Q345402*14 Q345B76*3 16Mn114*5.5 Q345B194*8 Q345B402*16 Q345B76*3.5 16Mn114*6 Q345B194*8 Q345426*12 Q345B76*4 Q345B114*6 Q345B194*10 Q345B426*14 Q345B76*4 16Mn114*6.5 Q345B194*12 Q345B426*16 Q345B76*5 Q345B114*7 16Mn203*10 Q345B426*18 Q345B76*6 16Mn114*7 Q345B203*12 Q345B426*20 Q345B83*6 16Mn114*8 16Mn219*6 Q345B530*8 Q345B83*8 Q345B114*10 Q345B219*8 Q345B530*10 Q345B89*4 16Mn114*16 16Mn219*10 Q345B530*14 Q345B89*4.5 Q345B121*5 Q345B219*12 Q345530*16 Q345B89*4.5 Q345B121*6 16Mn定尺219*12 Q345B530*18 Q345B89*5 Q345B121*6 16Mn219*14 Q345560*14 Q345B89*5 16Mn121*7 16Mn219*16 Q345B560*18 Q345B89*5 16Mn定尺121*12 Q345B245*8 Q345B560*20 Q345B89*5.5 Q345B133*6 Q345B245*10 Q345610*12 Q345B

Q215钢材化学成分Q215钢材牌号Q215钢材等级Q215钢材化学成分（质量分数）（%）CMnSiSP≤Q215A0.09~0.150.25~0.550.300.0500.045B0.045 Q215钢材力学性能Q215钢材牌号q295密度拉力强度MPa屈服点MPa伸长率（%）Q215335~45021531

炼钢炉炼成的钢水经过铸造后得到的产品就是钢坯。钢坯从制造工艺上主要可分为两种：模铸坯和连铸坯，目前模铸工艺已基本淘汰。    生产钢管所用的坯料，叫做管坯。通常，采用优质（或合金）的实心圆钢作管坯。某些管生产方式也有采用钢锭、连铸坯、锻坯、轧制方坯及离心浇铸的空心坯等做制管的坯料。一般情况下，管坯是指圆管坯。圆管坯的规格大小以实心圆钢的直径来表示。1 钢坯管坯加热工艺 对 130/185 工件计算切屑厚度 每次重磨后锯片寿命 锯片重磨次数 锯片更换用时 主驱动 AC 电机 芯轴旋转无级变速 AC 电机进给能力 无级变速进给 快速返回恒定值 中心润滑系统 刷扫装置 液压 3 条锯切系统 西门子控制系统 表示质量 Ra 平直度最大 毛刺高度 切屑长度公差 尺寸： 宽 长 0.1～0.15mm 10～20m2 8～10 3～5min 55kw 34～90rpm (180) 6.9kw 100～2000mm/min 8000mm/min 0.1kw 0.12kw 2×75kw S7 25µm 0.5/100 1.2mm ±1mm 大约 2850mm 大约 1200mm 大约 1920mm 大约 14000kg mm 高 每条坯总重 一个切断周期为 70 秒(包括夹紧、管坯切断、锯片返回、打开夹紧装置和管坯出料以及 切头、切尾的时间，但不包括管坯运输时间)。 3 台锯的最大生产能力为 50 万吨/年。管坯锯有一特殊的倒向装置(液压伺服装置)有利 于减振和提高锯的使用寿命(只在进给时起作用)。 锯床有两个夹紧装置分布于入出口(输入区 有辊道支撑保证弯坯的夹紧)锯切后入口端。夹紧打开保证锯片返回时不与坯子接触。 —进给锯齿轮 —锯齿轮减振， 由三个固定齿轮的减振组成， 作为可移动的减振避免了锯片相对于轴向 的摆动。 —刷扫装置 —在锯片的底部安装有一个驱动刷扫装置，清扫齿上的铁屑，不会影响锯片的寿命。 —锯片喷射润滑。 为了提高锯片的使用寿命， 高负载润滑剂的容器由空气雾化少量浇注 在锯片上，没有残留。 —锯片冷却装置。一个特殊的喷嘴，冷的空气-5oC 喷在锯片上。 锯切后的定尺坯经出口辊道和称重装置后拨至装料机前缓冲链(注：3#锯前有一尚需切 头的单倍尺坯上料台架，称重后有一回炉坯上料台架)，缓冲移送链将管坯运至装料机下辊 道前， 坯子由翻料钩从链上翻至辊道上称重合格的管坯由装料机装入环形炉， 称重不合格的 管坯由辊道运输至剔除台架前剔除。 2 环形炉简述 环形炉在热轧生产线中的作用是将管坯锯锯切之后的合格定尺管坯由常温 （20℃） 加热 到 1280±5℃以供穿孔机组进行穿孔工序。环形炉是目前世界上用于加热圆管坯的最理想的 工业炉炉型。 此炉型的特点是炉底呈环形， 在炉底驱动装置的作用下承载管坯由入料端旋转 至出料端， 再由出料机从出料炉门将加热好的管坯取出。 在管坯随炉底运动过程中通过炉墙、 炉顶等处的烧嘴加热达到合格的出料温度，并满足温度均匀性要求。 为了达到理想的加热质量， 从热工控制上将炉子从圆周方向上分成若干控制区， 依次形 成预热段、加热段、均热段，各段亦可再分若干控制区以提高控制精度，例如我厂环形炉就 分成 7 个控制区，预热段一个控制区，加热段四个控制区，均热段一个控制区，最后一个出 料区。各控制区按不同的温度进行控制，实现对管坯的合理加热，达到要求的加热质量。各 区的基本加热设备是烧嘴，烧嘴将助燃空气、燃料按合理的比例（空燃比）混合燃烧形成火 焰加热管坯。 其中燃料由管道系统供送， 助燃空气是由鼓风机 （助燃风机） 经由换热器加热， 再由空气管道分配至各区烧嘴参与燃烧。 而温度的调节由自动化控制系统通过调节管道上的 阀门开度实现燃料及配风的流量来实现。而燃料燃烧产生的烟气通过烟囱排入大气。炉底、 炉墙、烟道、烟囱等是由耐火材料砌筑而成的，以达到保温节能的效果。 与其它的炉型相比，环形炉具有以下优点： ★环形炉最适合加热圆管坯， 并能适应各种不同直径和长度的复杂坯料组成， 易于按管坯规 格的变化调整加热制度。 ★管坯在炉底上间隔放置，坯料能三面受热，加热时间短，温度均匀，加热质量好。 ★管坯在加热过程中随炉底一起转动， 与炉底之间没有相对运动和摩擦， 氧化铁皮不易脱落。 炉子除装出料门外无其它开口，严密性好，冷空气吸入少，因而氧化烧损较少。 ★炉内管坯可以出空，也可以留出不装料的空炉底段，便于更换管坯规格，操作调度灵活。 ★装料、出料和炉内运转都能自动运行，操作的机械化和自动化程度高。 环形炉的缺点是：炉子是圆形的，占用车间面积较大，平面布置上比较困难；管坯在炉 底上呈辐射状间隔布料，炉底面积的利用较差，单位炉底面积的产量较低。 目前，国际上 DALMING 厂环形炉中径为φ46m。ALGOMA 厂环形炉中径为φ36m， 国内宝钢环形炉中径为φ35m，成都无缝厂环形炉中径为φ20m，包头无缝厂环形炉中径为 φ35m，我厂一套环形炉中径φ48m，这些都是环形炉在无缝钢管厂使用的一些例证。 我厂管坯加热采用环形炉，中径 33.25m，年加热管坯量约为 50 万吨，造价近 4000 万人民 币。 3.2.1.1 1 布置 环形炉在生产线中的布置和作用 环形炉为高架布置，座落在+5m 平台上。炉体在 A-B 跨和 B-C 跨内，占据着两个跨。 从纵向看在 3 柱和 6 柱之间。 连铸管坯经冷锯切割成定尺管坯后， 管坯经由运输设备送至炉 子装料机夹钳下方， 装料机夹钳夹起管坯装入炉内。 加热好的管坯用出料机从炉内取出送至 穿孔工艺工序。 2 作用 轧管厂设置一座管坯加热炉，供连铸圆坯轧制前加热。 1) 生产任务 管坯规格：   钢坯管坯加热工艺 31 直径（mm）；200 210 150 长度（mm）：1122～4200 最大单重（kg）： 1040 注：管坯材质为低合金钢、合金钢。 2) 工艺要求 管坯加热温度：1260～1280℃ 允许温差：±5℃ 3.2.1.2 环形炉基本尺寸 炉底中心平均直径：33250mm 炉膛内部宽度:4800mm 炉底宽度：4350mm 炉膛高度：1800mm 装出料炉门夹角：14.47。 有效炉底面积：600.85m2 3、钢坯管坯加热工艺之三 炉子结构及辅助设备 结构概述： 环形炉由转动的炉底和固定的炉墙、炉顶组成。 图 3-1 环形炉运转示意图 管坯由装料机 A 送入环形炉并放置在炉底上，随炉底一起转动，在转动过程中，被安 装在炉子侧墙和炉顶的烧嘴加热，转动一圈后，由出料机 B 将被加热好的管坯取出。 环形炉炉内烟气按照与炉底转动相反的方向流动， 加热管坯后废气经由装料端内环侧墙上的 排烟口排除炉外。 1 具体的特点如下： 炉子的钢结构： 炉体外壳由轧制型钢焊接的柱梁和炉皮钢板组成。炉顶钢结构承载吊挂炉顶的耐火材 料。 2 环缝与水封：为了保证炉底运转良好,炉底和侧墙的内外环之间留有一定的缝隙,即环缝.考虑到炉子 工作时受热膨胀，炉子外环缝要比内环缝的缝隙稍大一些。 炉底和炉墙之间的环缝采用水封，水封系统由水封槽、活动刀和固定刀组成。活动刀安装在 炉墙上不动。在活动刀底部装有刮板，这样炉底在转动时，通过刮板，把水封槽内的氧化铁 皮和其它一些杂质刮到水封槽的漏斗处，最后通过漏斗清渣。 4、钢坯管坯加热工艺之四 隔墙： 在装料门和出料门之间的炉膛内设有一道隔墙 A， 其目的是减少低温管坯区对高温管坯 区及高温出炉管坯的吸热。及高温烟气直接进入低温区形成烟气短路。 在装料门后烟气出口前又设有一道隔墙 B，因为烟气出口处为负压，即有抽力。为了防止炉 膛从装料门吸入大量的冷空气，造成热耗和烧损的增加，就设置了这道隔墙 B。出料段与均 热段间设有一道隔墙 C,起到了隔离均热段与出料段,提高加热均匀性， 进一步防止烟气短路。 炉门及其它 炉子四周设有必要的检修门和观察门。 操作平台， 走道和梯子可以通达所有的烧嘴和阀 门处。 3.2.2.2 1 炉子机械 装出料机 钢坯管坯加热工艺 33 1) 结构 装出料机都是由一个固定的钢架和安装在钢架上的操作小车组成， 操作小车又由带有夹 钳的机械臂的提升装置组成。操作小车的运动用电机驱动，夹钳用液压缸开闭，所有暴露在 炉膛高温下的机械部件都采用水冷，装有绞盘，在紧急情况下把机械臂从炉内退出。 为了使夹钳夹管坯平稳，最大行程为 7600mm，且出料机夹钳可以左右摆动。扒渣机设在装 料机之间负责扒除炉底氧化铁皮积渣。 2) 动作描述 装出料机可以同步工作，也可以分别工作，所有动作都是由液压传动来完成的。装出料 机的动作可以近似看为一个矩形， 机械臂提升 前进 下降 夹钳打开 （夹紧夹钳） 3) 提升 后退 技术参数： 起重能力：1040kg 运行速度：>1m/s 运送行程：7600mm 动作频率：180 次/小时 2 炉底装置 1) 结构 环形炉的中枢部分是在炉底结构。 转动炉底是由一个型钢制成的双层钢架， 上下两层钢 架之间不是紧固连接的。上层钢架承载炉底耐火材料，下层钢架的横断面呈梯形，可把传动 设备、支撑辊、定心辊布置在炉底两侧，有利于设备的更换和维修。 2) 转动机械 环形炉通过均匀分布在炉底圆周上的两台液压马达销轮和柱销装置驱动， 柱销安装在炉 底下层钢架的外环侧。 炉底可以反向转动， 通过液压靠紧装置可以保持传动销轮和柱销之间 始终能良好的咬合。 表 3-1 每步转动距离 mm 炉内根数 每步周期(最小)S 布料排数 3 1) 定心辊和支撑辊 定心辊 为了使炉底以一个固定中心转动，采用了水平定心辊来实现定心，即沿圆周设有 12 组 321.4 313 20 单排或交错 带弹簧压紧装置的弹簧式定心辊。 定心是从内环方向向外顶住炉底下层钢架来实现。 定心力 的大小通过调节弹簧的压力来实现。 2) 4 支撑辊 整个炉底由 96 个锻钢滚轮支撑。 炉门开闭机械 装料门、出料门和清渣门用加筋的钢结构制成，内衬以浇注料,传动采用液压缸,炉门的开闭与装、出料机操作连锁。 2 炉子的供热与燃烧系统 概述 环形炉烧天然气,按照加热制度分为七个控制段供热,从装料门开始,第一段为预热段,中间四段为加热段,第六段为均热段， 第七段为出料段,预热段、 加热段侧墙上均装有德国 Krom 公司的高速型侧烧嘴,均热段和出料段炉顶装有德国 Krom 公司的平焰顶烧嘴。 2 燃烧系统的组成及设备性能 燃烧系统由一台助燃风机、空气管道、一台烟气稀释风机、一台空气换热器、一套燃气 分配系统和烧嘴形成。构成燃烧系统的这些设备，保证了燃料、助燃空气通过烧嘴达到正常 燃烧的目的。下面分别介绍： 1) 助燃空气鼓风机(1 台) 鼓风机的作用 是提供足够的助燃空气。 直联离心式 风量 60000m3/h 风压 转速 2) 功率 烟气稀释风机(1 台) 12000pa 1450r/min 355kw(10kv 50HZ)作用：烟气出炉温度很高时（850℃）,则起动稀释风机，向烟气内鼓入冷空气，这样烟 气温度就下降，保证烟气到达换热器处的温度最高值低于允许温度（930℃），保护换热器 不至于被烧毁.这种操作是自动进行的，随烟气温度的升降自动开闭稀释风机。 性能： 型式 直联离心式 风量 风压 转速 功率 3 空气预热器 1) 作用 烟气出炉温度很高近 1000℃，具有很高的热能，把这部分能量传给空气，这样便可回 收一定的热能，达到节能，提高热效率的目的。 2) 结构 换热器是由许多无缝钢管组成的。钢管内部走空气，换热器置于烟道内，这样，钢管内 12000m3/h 1960pa 1450r/min 15kw的空气就被加热了。 由于烟气的走向和空气的走向是相反方向的， 所以叫做逆流管状换热器。

Q275钢管化学成分Q275钢管牌号Q275钢管等级Q275钢管化学成分（质量分数）（%）CMnSiSP≤Q275—0.28~0.380.50~0.800.350.0500.045 Q275钢管力学性能Q275钢管牌号拉力强度MPa屈服点MPa伸长率（%）Q275490~63027520

Q345B无缝钢管与16mn低合金管16mn低合金管材质：16Mn，Q345B材质：16Mn，Q345B无缝钢管钢管材质：16Mn，Q345B材质：16Mn，Q345B规格 材质规格 材质规格 材质规格 材质22*2.5 16Mn89*6 Q345B133*7 Q345B245*12 Q345B25*2.5 16Mn89*6 Q345B133*7 16Mn273*8 Q34525*4.5 16Mn89*6.5 16Mn133*8 Q345B273*10 Q34532*3 16Mn89*7 Q345B133*9 Q345B273*10 Q345B42*4 16Mn89*7 16Mn133*10 Q345B273*12 Q345B45*3 Q345B89*8 16Mn133*10 16Mn273*14 Q345B45*4 16Mn89*10 16Mn140*6 Q345B299*8 Q345B50*4 16Mn89*12 Q345B140*8 Q345B299*10 Q34550*5 Q345B89*13 Q345B146*8 Q345B299*12 Q345B51*4.5 16Mn95*4 Q345B159*6 Q345B299*16 Q345B57*3.5 Q345B95*5 Q345B159*10 Q345B325*8.5 Q34557*4 16Mn95*5.5 Q345B159*12 Q345B325*12 Q345B57*5 16Mn95*8 Q345B168*6 Q345325*14 Q345B60*3 16Mn102*5.5 Q345B168*7 Q345325*16 Q345B60*3.2 16Mn102*6 Q345B168*8 Q345351*9 Q345B60*5 Q345B102*7 Q345B168*8 Q345B351*10 Q345B63.5*5 16Mn102*14 16Mn168*10 Q345B351*14 Q34565*4 16Mn102*16 16Mn168*12 Q345B351*14 Q34567*5.5 16Mn108*4 16Mn180*6 Q345B351*16 Q345B68*3 16Mn108*5 16Mn180*8 Q345356*8 Q34570*5 Q345B108*7 16Mn180*8 Q345B377*14 Q345B70*7 16Mn108*8 16Mn180*10 Q345B402*9 Q345B73*3.5 16Mn108*13 16Mn180*12 Q345B402*10 Q345B73*5 Q345B114*4 16Mn180*16 Q345B402*12 Q345B73*6.5 16Mn114*5 Q345B194*6 Q345402*14 Q345B76*3 16Mn114*5.5 Q345B194*8 Q345B402*16 Q345B76*3.5 16Mn114*6 Q345B194*8 Q345426*12 Q345B76*4 Q345B114*6 Q345B194*10 Q345B426*14 Q345B76*4 16Mn114*6.5 Q345B194*12 Q345B426*16 Q345B76*5 Q345B114*7 16Mn203*10 Q345B426*18 Q345B76*6 16Mn114*7 Q345B203*12 Q345B426*20 Q345B83*6 16Mn114*8 16Mn219*6 Q345B530*8 Q345B83*8 Q345B114*10 Q345B219*8 Q345B530*10 Q345B89*4 16Mn114*16 16Mn219*10 Q345B530*14 Q345B89*4.5 Q345B121*5 Q345B219*12 Q345530*16 Q345B89*4.5 Q345B121*6 16Mn定尺219*12 Q345B530*18 Q345B89*5 Q345B121*6 16Mn219*14 Q345560*14 Q345B89*5 16Mn121*7 16Mn219*16 Q345B560*18 Q345B89*5 16Mn定尺121*12 Q345B245*8 Q345B560*20 Q345B89*5.5 Q345B133*6 Q345B245*10 Q345610*12 Q345B

b30白铜详细介绍材料名称：B30 普通白铜 标准：（GB/T 5231-2001)化学成分：   镍+钴 Ni+Co：29.0-33.0   铁 Fe：0.9   锰 Mn：1.2   硅 Si：0.15   铅 Pb：0.001   硫 S：0.01   碳 C：0.05   磷 P：0.006   铜 Cu：余量 力学性能： 抗拉强度 σb （MPa）：（热轧）390～540; （冷拉）钢材厚度或直径 8～20时：530～755; ＞20～30时：510～735; ＞30时：490～685伸长率 δ5 （％）：（热轧）≥22;（冷轧）≥7．0断面收缩率 ψ （％）：（热轧）≥36硬度 ：（热轧）≤170HB;（冷拉钢）152～217HB热处理工艺： 工艺优良 以上就是b30白铜详细信息，更多内容请详见上海 有色金属 网 

钢坯是炼钢炉炼成的钢水经过铸造后得到的产品。 　　钢坯从制造工艺上主要可分为两种：模铸坯和连铸坯，目前模铸工艺已基本淘汰。 　　从外形上主要分为两种： 钢坯按形状及用途分类　　板坯：截面宽、高的比值较大，主要用来轧制板材。  　　方坯：截面宽、高相等，或差别不大，主要用来轧制型钢、线材。 产品规格（mm） 钢坯按形状及用途分类材质 定尺（M） 执行标准  　1、方坯  150×150×7800 HRB335 6-12 GB700-2006 150×150×6000 HRB335  150×150×9700 HRB335  150×150×9000 Q235  135×135×9800 Q235  135×135×9000 Q235  135×135×9000 16Mn  135×135×9000 16Mn  135×135×9800 16Mn  150×150×6000 B7  135×135×9000 B7  135×135×9000 12LW  150×150×8600 55Q  135×135×9000 24Mn2k  　2、矩型坯 65×225×9000 Q235 6-12 GB1519-88  180×275×9000 Q235  180×275×6000 Q235  180×275×6000 16Mn  　3、板坯 150×1200×6000 Q235 5-9 GB699-88  150×1200×5300  150×1120×5000  150×1120×5900  180×1200×6000  200×1200×4600  200×1200×6000  150×1000×4100  150×1100×4700  150×1250×6000 Q215  150×1120×5000 Q215  150×1200×6000 16Mn  150×1100×5700 16Mn  150×1100×6000 16Mn  150×1200×6000 12LW  产品 　　　钢坯规格 　　　断面尺寸mm　定尺m 方坯 　　　120×120、135×135、150×150　3～12 板坯 　　　厚度：150、180、200　　　宽度： 1000～1200　4.5～6

Q195钢管化学成分q195化学成分如下Q195钢管牌号Q195钢管等级Q195钢管化学成分（质量分数）（%）CMnSiSP≤Q195—0.06~0.120.25~0.500.300.0500.045     Q195钢管力学性能Q195钢管牌号q195力学性能拉力强度Mpaq195力学性能屈服点MPaq195力学性能伸长率%Q195315~43019533q195板材标准可以看上图

q345钢管化学成分q345钢管牌号等级q345钢管化学成分(质量分数)(%)C ≤MnSi ≤P ≤S ≤VNbTiAI≥Cr ≤Ni ≤    Q345A  0.201.00 ~ 1.60    0.550.0450.0450.02 ~ 0.150.015 ~ 0.0600.02 ~ 0.20－－－B0.0400.040－－－C0.0350.0350.015－－D0.180.0300.0300.015－－E0.0250.0250.015－－ q345钢管力学性能q345钢管牌号等级拉力强度MPa屈服点MPa伸长率（%）    Q345A    470~630    345    22BCDE

q460钢材化学成分q460钢材牌号等级q460钢材化学成分(质量分数)(%)C ≤MnSi ≤P ≤S ≤VNbTiAI≥Cr ≤Ni ≤  Q460C  0.201.00 ~ 1.70  0.550.0350.0350.02 ~ 0.200.015 ~ 0.0600.02 ~ 0.200.0150.700.70D0.0300.0300.0150.700.70E0.0250.0250.0150.700.70 q460钢材力学性能q460钢材牌号等级拉力强度MPa屈服点MPa伸长率（%）Q460A    550~720    460    17

Q255钢材化学成分Q255钢材牌号Q255钢材等级Q255钢材化学成分（质量分数）（%）CMnSiSP≤Q255A0.18~0.280.40~0.700.300.0500.045B0.045 Q255钢材力学性能Q255钢材牌号拉力强度MPa屈服点MPa伸长率（%）Q255410~55025524

Q295钢管化学成分Q295钢管牌号等级Q295钢管化学成分(质量分数)(%)C ≤MnSi ≤P ≤S ≤VNbTiAI≥Cr ≤Ni ≤Q295A  0.160.08 ~ 0.50  0.550.0450.0450.02 ~0.150.015 ~0.0600.02 ~0.20－－－B0.0400.040－－－ Q295钢管力学性能Q295钢管牌号等级拉力强度MPa屈服点MPa伸长率（%）Q295A390~57029523B

Q420钢管化学成分Q420钢管牌号等级                                        Q420钢管化学成分(质量分数)(%)C ≤MnSi ≤P ≤S ≤VNbTiAI≥Cr ≤Ni ≤    Q420A    0.20  1.00 ~ 1.70    0.550.0450.045  0.02 ~ 0.20  0.015 ~ 0.060  0.02 ~ 0.20－0.400.70B0.0400.040－0.400.70C0.0350.0350.0150.400.70D0.0300.0300.0150.400.70E0.0250.0250.0150.400.70   Q420钢管力学性能Q420钢管牌号等级拉力强度MPa屈服点MPa伸长率（%）    Q420A    520~680    420    18BCDE

YB235-70标准的意义是：地质钻探用钢管 YB235-70标准的用途是：供地质部门进行岩心钻探使用的钢管，按用途可分为钻杆、钻铤、岩心管、套管和沉淀管等 YB235-70标准的生产厂家：  生产单位有成都无缝钢管厂、鞍钢、包钢、本钢、宝钢、安钢、烟台鲁宝、大连钢厂、西宁特钢、衡阳钢厂、冶钢

Q390钢管化学成分Q390钢管牌号等级Q390钢管化学成分(质量分数)(%)C ≤MnSi ≤P ≤S ≤VNbTiAI≥Cr ≤Ni ≤    Q390A    0.20  1.00 ~ 1.60    0.550.0450.045  0.02 ~ 0.20  0.015 ~ 0.060  0.02 ~ 0.20－0.300.70B0.0400.040－0.300.70C0.0350.0350.0150.300.70D0.0300.0300.0150.300.70E0.0250.0250.0150.300.70     Q390钢管力学性能Q390钢管牌号等级拉力强度MPa屈服点MPa伸长率（%）Q390A    490~650    390    20BCDE

2B11铝合金特性及适用范围 　　2B11铝合金为铆钉用合金。2B11铝合金具有中等剪切强度，可热处理强化，在退火、刚淬火和热态下塑性尚好，铆钉必须在淬火后2h内铆接。 　　2B11力学性能 　　抗剪强度 τ (MPa)：≥235 　　注 ：线材固溶热处理后自然时效至基本稳定状态抗剪性能 　　试样尺寸：所有线材直径 　　热处理规范 　　1)完全退火：加热390～430℃；随材料有效厚度不同，保温时间30～120min；以30～50℃/h速度随炉冷至300℃下，再空冷。 　　2)快速退火：加热350～370℃；随材料有效厚度不同，保温时间30～120min；空冷。 　　3)淬火和时效：淬火495～505℃，水冷；自然时效室温，96h。 　　2B11铝合金状态：铆钉用铝及铝合金线材 (T4态)

主要特征及应用范围： 　　铆钉用合金。剪切强度和2A02相当，其他性能和2B11相似，但铆钉必须在淬火后20min内铆接，故工艺困难，因而应用范围受到限制. 　　力学性能：　　抗剪强度 τ (MPa)：≥265　　注 ：线材固溶热处理后自然时效至基本稳定状态抗剪性能　　试样尺寸：所有线材直径　　热处理规范： 　　1)完全退火：加热390～430℃;随材料有效厚度不同，保温时间30～120min；以30～50℃/h速度随炉冷至300℃下，再空冷。 　　2)快速退火：加热350～370℃；随材料有效厚度不同，保温时间30～120min；空冷。 　　3)淬火和时效：淬火490～500℃，水冷；自然时效室温96h。　　合金状态：铆钉用铝及铝合金线材。

地质钻探用管 YB235尺寸公差地质钻探用管 YB235标准 地质钻探用管 YB235外径公差 地质钻探用管 YB235壁厚公差YB 235 D≤89.5 ±0.8%  D>89.5 ±1% 按标准地质钻探用管 YB235机械性能/化学成份标准 纲级 抗拉强度(MPa) 屈服强度(MPa) 延伸率(%) P SYB 235 DZ40 637 373 14 ≤0.040 0.045DZ50 686 490 12

铝合金5B05力学性能： 　　抗剪强度 τ (MPa)：≥157 　　注 ：线材热处理不强化抗剪性能　　●热处理规范：　　快速退火：加热350～410℃;随材料有效厚度的不同,保温时间30～120min;空或水冷。 　　状态 ：铆钉用铝及铝合金线材 (HX8态）[1] 　　热处理工艺：快速退火：加热350～410℃;随材料有效厚度的不同,保温时间30～120min;空或水冷。 　　状态 ：铆钉用铝及铝合金线材 (HX8态)

耐诺氧化锆球(NanorZr-95B): 采用氧化钇作稳定，干粉等静压成形，烧结定相的工艺制成。PPM级的磨耗和优异的抗剪切性特别适合篮式砂磨机、立式搅拌磨、卧式滚动磨、振动磨等设备对拒绝污染的浆料和粉料的湿法和干法的超细分散和研磨。 氧化锆含量: 95%, 氧化钇含量: 5%, 比 重: >6.0kg/dm3, 散 重: >3.6kg/L, 莫 氏 硬度: 9, 维 氏 硬度: >1200kg/mm2, 断 裂 韧性: 10Mpa.m1/2 弹 性 模量: 200Gpa, 粒 径: 3-50mm, 颜 色: 奶白, 包 装: 25kg/桶.

材料名称：2B12 旧称：LY9 　　标准：GB/T 3196-2001 　　化学成分： 　　硅Si：0.50 　　铁Fe: 0.50 　　铜Cu：3.8-4.5 　　锰Mn：0.30-0.7 　　镁Mg：1.2-1.6 　　锌Zn：0.10 　　钛Ti：0.15 　　铝Al：余量 其他： 　　单个:0.05；合计:0.10

北京化工冶金研讨院组成的353E和365B树脂，为乙烯－二的骨架大孔结构双官能团阳离子交流树脂。它的强碱性季胺基团含量远大于弱碱性叔胺基团，总交流容量、比表面积、机械强度和粒径都超越前苏联AM－2B树脂。经过比照实验，365B树脂金的吸附容量比353E树脂高17%，选择性高16%，也优于AM－2B树脂。故选用365B树脂从化矿浆中进行提金实验。 一、树脂浆法吸附 实验规划为日处理矿石0.5t，树脂的吸附是在串联的10只有用容积为35L的空气拌和槽中进行接连逆流吸附。矿浆浓度45%，溶液含金95mg∕L，树脂在每只槽内的矿浆中含量（体积比）为5%，矿浆在每个槽内的均匀停留时间1h，树脂与矿浆流量的体积比为1∶83。经10级接连逆流吸附，金的吸附回收率为99.5%，载金树脂（以干树脂计）吸附金量21.5mg∕g。 二、载金树脂的解吸 解吸选用解吸柱，研讨了从载金树脂上解吸金的若干种计划。鉴于硫酸－分步解吸法早已成功地在前苏联出产中广为选用，本实验是在室温下选用如下的分步解吸作业： （一）用30g∕L NaCN液洗刷除掉Cu、Fe； （二）树脂经水洗后，用30g∕L H2SO4液洗刷，使树脂转变为HSO4－、SO42－型，一起使大部分Zn、Ni等从树脂中洗脱出来； （三）用80g／L SC（NH2）2和30g∕L H2SO4混合液在温度15℃解吸Au、Ag； （四）解吸金后的树脂，经水洗后再用30g∕L NaOH液洗刷出SC（NH2）2和其他杂质，并经水洗后回来再用于吸附进程。 图1是本工艺的解吸曲线图，它具有极好的典型峰值。在进步条件下，经45min经过10个床体积的解吸液，金的解吸率达98.6%。其间，从解吸柱流出的第1.5～4.5个床体积（共3个床体积）的解吸液中含金达1640mg∕L，可作为合格贵液送电积提金。图1  365B载金树脂金的解吸曲线 三、解吸液的电积提金 金的电积运用3只串联的隔阂电解槽；每个槽用离子交流膜隔成若干个阴极区和阳极区。阳极用石墨板，阴极甩钛板。阳极液为30g∕L H2SO4液。含金阴极液在电解体系内的停留时间为10h。面积电流在15和20A∕m2时，金的阴极电堆积回收率分别为98.98%和99.57%。 阴极堆积物经火法熔炼铸成合质金锭，含金档次达91.20%。整个作业进程中各级产品的金属含量列于表1。 表  365B树脂提金进程中各级产品的组分产品金属含量∕mg·g－1AuAgCuZnNiFe载金树脂21.52.037.25.410.42未化验NaCN洗刷后树脂20.80.573.700.15未化验H2SO4洗刷后树脂21.21.30.11＜0.1未化验SC（NH2）2解吸金后树脂0.30.10.240.10＜0.1未化验解吸产出的贵液1640242265.66.939合质金锭／%91.205.62.30.50.2

武钢榜首炼钢厂(以下简称一炼钢)2005年冷镦钢产量近5万t，典型钢种有SWRM6、SWRM8、SWRM10等。浇铸该类钢种时，铸坯表面振痕深度达0.5～0.7mm，一起在振痕谷底处常伴有肉眼可见微裂纹。这些表面缺点严重影响了铸坯的质量，影响了冷镦钢的后续加工功能。现在对冷镦钢连铸时铸坯表面振痕问题的研讨很少，尤其是碳含量较低的SWRM6、SWRM8等钢种。因而有必要结合一炼钢的实践出产工艺条件，找呈现在冷镦钢连铸时构成铸坯表面振痕缺点的首要原因，进步铸坯的表面质量。 1方坯表面振痕描摹及构成机理　　一炼钢出产的SWRM8方坯表面振痕状况。坯样取自2号连铸机，浇注条件是：过热度3O℃，拉速1.6m／min，二冷选用强冷准则。可以看出，SwRM8方坯表面首要有以下缺点。(1)振痕。凹形深振痕，均匀深达0.5mm，且振痕曲折。(2)洼陷。接近角部区域呈现纵向洼陷，最深处达3.5～4.0mm，且洼陷部位有粘渣现象。经过对不同连铸条件下的铸坯表面振痕进行金相分析，最常见的振痕形状首要有两类：洼陷状振痕和带钩状振痕。　　为了改进铸坯表面质量，减小振痕深度，人们对维护渣存在状况下的连铸坯振痕构成的原因进行了深人详尽的研讨，在弯月面处，因为钢液的过热度及钢液对流的影响，弯月面处0.3s期间内构成的凝结坯壳或许表现为刚体，也或许表现为液体的性质，即具有流变性。因为结晶器的振荡，弯月面区域的维护渣中发生压力。在负滑移期间，结晶器向下振荡的速度大于拉坯速度时，弯月面会被维护渣道中构成的正压力面向钢液中，在正滑脱期间，当初始凝结坯壳强度不大，维护渣中构成的负压力和动摇钢液的惯性力将坯壳面向结晶器内壁，导致初始凝结坯壳曲折或堆叠，构成不带钩状的振痕。当初始凝结坯壳的厚度较大，强度高的时分，初始凝结坯壳不能面向结晶器内壁，因而钢液会掩盖在弯月面上，构成一种带钩状的振痕。2振痕缺点构成原因分析　　针对一炼钢出产的SWRM8方坯振痕状况，振荡参数不合理(振幅大、频率低)，负滑脱时振痕间长，维护渣理化功能不适宜等振痕曲折滑不良，摩擦阻力大使振痕沿拉坯方向曲折。2.1振痕构成的影响要素　　振痕距离和振痕深度是衡量振痕的重要参数。因而，考虑连铸坯振痕的影响要素时，应别离考虑这两个参数。一起，很多研讨标明，无论是低碳钢仍是中碳钢，当振痕距离增大时，振痕的深度随之增大。合理的操控振痕距离对操控振痕深度有重要作用。2.2振荡参数对振痕的影响　　连铸过程中铸坯的振痕都与结晶器的振荡参数密切相关，其振荡模式首要为正弦振荡。振痕构成机理及试验研讨均标明振痕是在负滑脱期间发生的，负滑脱时刻越长，振痕的深度就越大，因而操控负滑脱时刻的长短，可以有用地操控振痕的形状。3结晶器振荡参数的优化3.1现行振荡参数特色(1)跟着拉速的不断进步，负滑脱率在不断的下降；(2)拉速的不断进步，对负滑脱时刻的影响不大；(3)拉速的进步，使得结晶器导前显着增加。3.2结晶器振荡参数的断定　　在实践振荡过程中，断定适宜的结晶器振荡基本参数振幅和频率厂是取得高质量的铸坯的要害，断定上述参数的首要准则是以取得合理的工艺参数为条件，可以依据工艺要求调理振幅、频率得到。断定工艺参数的总准则是应尽量减小铸坯表面振痕深度及改进结晶器和坯壳之间的光滑，这便要求可以取得较小的负滑脱时刻，较大的正滑脱时刻，尽量小的正滑脱速度差，足够大的负滑脱量NSA以及恰当的负滑脱速度比率NS和负滑脱时刻比率NSR。3.3振荡参数优化计划及作用　　依据以上对结晶器振荡工艺参数与基本参数联系的分析，结合振痕构成机理可知：要削减振痕深度，就要减小负滑脱时刻，可经过减小振程或许进步振频，或许两个参数都恰当改动的方法来完成。4结语　　依据一炼钢的状况，提出了3种振荡参数优化计划，经过核算比较分析，再结合结晶器振荡参数断定准则，得最佳计划。计划在整个拉速范同内均满意条件，负滑脱时刻保持在0.10s左右，在作业拉速规模(1.2～1.8m／min)内，负滑脱率在28～30%之间，结晶器导前1.5～2.5mm，振痕距离8～11mm。除结晶器导前稍微偏小外，其他工艺参数均在最佳取值规模内，且负滑脱时刻较现行振荡参数状况下缩短约0.02S，能有用减小振痕深度。选用计划3后，经过5个浇次的取样分析，方坯表面振痕得到显着改进，均匀振痕深度为0.372mm。

2B11化学成份： 　　铝 Al ：余量 　　硅 Si ：≤0.50   　2B11硬铝 　　铜 Cu ：3.8～4.5 　　镁 Mg：0.40～0.8 　　锌 Zn：≤0.10 　　锰 Mn：0.40～0.8 　　钛 Ti ：≤0.15 　　铁 Fe： 0.000～0.500 　　注：单个:≤0.05;合计:≤0.10

5b05铝合金介绍 　　材料名称：5B05 旧称：LF10　　标准：GB/T　　主要特征及应用范围： 　　为铝镁系防锈铝（5B05的含镁量稍高于5A05）,强度与5A03相当，热处理不能强化;退火状态塑性高，半冷作硬化时塑性中等;用氢原子焊、点焊、气焊、氩弧焊时焊接性能尚好; 抗腐蚀性高,可切削性能在退火状态低劣，半冷作硬化时可切削性尚好，制造铆钉时需进行阳极化处理。     化学成分化学成分： 　　硅Si：0.40　　铁Fe: 0.40　　铜Cu：0.10　　锰 Mn:0.20-0.6　　镁Mg：4.7-5.7　　钛Ti：0.15　　硅+铁Si+Fe：0.6　　铝Al：余量 　　其他： 　　单个：0.05 合计：0.10

合得奖号 成 分ANSI ASTM UNS Si Fe Cu Mn Mg Ni Zn Sn Ti 除铝以外的其他成分(总量) 铝AI360.0 SG100B A03600 9.0-10.0 2.0 0.6 0.35 0.40-0.60 0.50 0.50 0.15   0.25 余量A360.0 SG100A A13600 9.0-10.0 1.3 0.6 0.35 0.40-0.60 0.50 0.50 0.15   0.25 余量380.0 SC84B A03800 7.5-9.5 2.0 3.0-4.0 0.50 0.10 0.50 3.0 0.35   0.50 余量A380.0E SC84A A13800 7.5-9.5 1.3 3.0-4.0 0.50 0.10 0.50 3.0 0.35   0.50 余量383.0E SC102A A03830 9.5-11.5 1.3 2.0-3.0 0.50 0.10 0.30 3.0 0.15   0.50 余量384.0E SC114A A03840 10.5-12.0 1.3 3.0-4.5 0.50 0.10 0.50 3.0 0.35   0.50 余量390.0 SC174A A03900 16.0-18.0 1.3 4.0-5.0 0.10 0.45-0.65   0.10   0.20 0.20 余量B390.0 SC174B A23900 16.0-18.0 1.3 4.0-5.0 0.50 0.45-0.65 0.10 1.5   0.10 0.20 余量392.0 S19 A03920 18.0-20.0 1.5 0.40-0.80 0.20-0.60 0.80-1.20 0.50 0.50 0.30 0.20 0.50 余量413.0 S12B A04130 11.0-13.0 2.0 1.0 0.35 0.10 0.50 0.50 0.15   0.25 余量A413.0 S12A A14130 11.0-13.0 1.3 1.0 0.35 0.10 0.50 0.50 0.15   0.25 余量C433.0 S5C A34430 4.5-6.0 2.0 0.6 0.35 0.10 0.50 0.50 0.15   0.25 余量518.0 G8A A05180 0.35 1.8 0.25 0.35 7.5-8.5 0.15 0.15 0.25   0.25 余量